Abstract:With a better balance among good mechanical performance, high freedom of design, and low material and manufacturing cost, chopped carbon fiber chip reinforced sheet molding compound (SMC) composites show great potential in different engineering applications. In this paper, bending fatigue behaviors of SMC composites considering the heterogeneous fiber orientation distributions have been thoroughly investigated utilizing both experimental and computational methods. First, four-point bending fatigue tests are performed with designed SMC composites, and the local modulus is adopted as a metric to represent the local fiber orientation of two opposing sides. Interestingly, SMC composites with and without large discrepancy in local modulus of opposing sides show different fatigue behaviors. Interrupted tests are conducted to explore the bending fatigue failure mechanism, and the damage processes of valid specimens are also closely examined. We find that the fatigue failure of SMC composites under four-point bending is governed by crack propagation instead of crack initiation. Because of this, the heterogeneous local fiber orientations of both sides of the specimen influence fatigue life. The microstructure of the lower side shows a direct influence while that of the upper side also exhibiting influence which becomes more prominent for high cycle fatigue cases. Furthermore, a hybrid micro-macro computational model is proposed to efficiently study the cyclic bending behavior of SMC composites. The region of interest is reconstructed with a modified random sequential absorption algorithm to conserve all the microstructural details including the heterogeneous fiber orientation, while the rest of the regions are modeled as homogenized macro-scale continua. Combined with a framework to capture the progressive fatigue damage under cyclic bending, the bending fatigue behaviors of SMC composites are accurately captured by the hybrid computational model comparing with our experimental analysis.

Experimental investigation and multiscale simulation on the bending fatigue of 2D SiCf/SiC composites

Experimental investigation and multiscale simulation on the bending fatigue of SiCf/SiC composite vanes

Experimental and Numerical Study on the Bending Behavior of Satin-Woven SiCf/SiC Composites

Multi-scale analysis and experimental research for turbine guide vanes made of 2D braided SiCf/SiC composites in high-cycle fatigue regime

Experimental and Numerical Analysis of Progressive Damage of SiCf/SiC Composite under Three-Point Bending

Experimental and computational analysis of bending fatigue failure in chopped carbon fiber chip reinforced composites

Degradation analysis on high-cycle bending fatigue for woven SiC/SiC composites based on Wiener process model

Prediction of fatigue limit stress in C/SiC composites: Effect of stochastic load spectrum

Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

Behavior of Two-Dimensional C/SiC Composites Subjected to Thermal Cycling in Controlled Environments

Multi-scale modeling and tensile failure prediction of 3D needled C/C-SiC composites considering real microstructure

Damage Analysis of a SiCf/SiC Ceramic Matrix Composite under Stepwise Fatigue Loading with Acoustic Emission

Fatigue life prediction considering individual modulus for unidirectional needled C/SiC composites under variable amplitude loading

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Experimental and numerical studies on low-velocity impact of laminated C/SiC structures

Experimental Investigation on Fatigue Property at Room Temperature of C/SiC Composites Machined by Rotary Ultrasonic Milling

Piecewise damage model for SiC/SiC composites with multilevel experimental validation

In situ investigation of failure in 3D braided SiCf/SiC composites under flexural loading

Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air

A Quantitative Representation of Damage and Failure Response of 3D Textile SiC/SiC Ceramics Matrix Composites Subjected to Flexural Loading

Fatigue behavior and damage analysis of PIP C/SiC composite