Abstract:Composite mechanical joints are extensively used and becoming crucial components for primary and secondary structures in industry. Considerable efforts have been contributed to the failure behavior of resin matrix laminate composite bolt joint, but few ones refer to carbon matrix woven composites. In current work, a comprehensive experimental and numerical research on the failure behavior for satin woven carbon/carbon composites under pin-loading, which is the typical loading case for mechanical joint, was presented. Seven types of specimens with different configuration were tested to evaluate the influence of the geometry on the failure modes. The testing results stated that, with the increasing of width-to-hole diameter ratio (W/D) and edge distance-to-hole diameter ratio (E/D), the net tension and shear out failure transformed into the bearing failure respectively, while hole diameter-to-thickness ratio (D/t) hardly affect the failure mode. For a further exploration for damage mechanism of the acceptable bearing failure in engineering, damage accumulation and evolution were assessed combining numerical simulation and acoustic emission monitoring. In view of the complexity of satin woven framework, the hierarchical multiscale numerical strategy from micro-to macro-level was proposed to obtain the material mechanical performance. In order to acquire reliable prediction and consider the effects of the uncertainty sources on composite properties, the model geometry reconstruction was performed using X-ray tomography. Meanwhile, the fiber and void random distributions were determined via the Random Sequential Adsorption algorithm. The Murakami-Ohno damage theory was adopted to characterize the damage propagation. It is concluded that, the numerical prediction agreed with the testing results reasonably well, and the main damage mechanism during the bearing failure included matrix cracking, yarns pulling-out and yarns fracture matching various amplitude ranges of acoustic emission signals.

Experimental investigation and multiscale simulation on the bending fatigue of SiCf/SiC composite vanes

Experimental investigation and multiscale simulation on the bending fatigue of 2D SiCf/SiC composites

Progressive failure analysis of 2D woven composites at the meso-micro scale

Multi-scale analysis and experimental research for turbine guide vanes made of 2D braided SiCf/SiC composites in high-cycle fatigue regime

Experimental and computational analysis of bending fatigue failure in chopped carbon fiber chip reinforced composites

Experimental and Numerical Analysis of Progressive Damage of SiCf/SiC Composite under Three-Point Bending

Experimental and Numerical Study on the Bending Behavior of Satin-Woven SiCf/SiC Composites

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Multi-scale modeling and tensile failure prediction of 3D needled C/C-SiC composites considering real microstructure

Degradation analysis on high-cycle bending fatigue for woven SiC/SiC composites based on Wiener process model

Simulation of failure behavior of 2.5D SiC/SiC variable thickness dovetail joint structures based on mesoscale model

Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

Characterization and modeling of fatigue behavior of chopped glass fiber reinforced sheet molding compound (SMC) composite

Multiscale analysis method and experiments for the transverse mechanical property of unidirectional fiber-reinforced composites

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Progressive failure analysis of needle-punched C/SiC composites based on multiscale finite element model

Prediction of fatigue limit stress in C/SiC composites: Effect of stochastic load spectrum

Experimental and numerical studies on low-velocity impact of laminated C/SiC structures

Multiscale Numerical Scheme on Shear Failure Feature of 3dowc/cs Bar Incorporating Microlevel Uncertainties and Coupled Constitutive Behavior

Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Flexural fatigue behavior of novel co-curing damping composite structures