Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Yanfeng Zhang,Zhengong Zhou

DOI: https://doi.org/10.1016/j.ijmecsci.2022.107129

IF: 7.3

2022-01-01

International Journal of Mechanical Sciences

Abstract:Composite mechanical joints are extensively used and becoming crucial components for primary and secondary structures in industry. Considerable efforts have been contributed to the failure behavior of resin matrix laminate composite bolt joint, but few ones refer to carbon matrix woven composites. In current work, a comprehensive experimental and numerical research on the failure behavior for satin woven carbon/carbon composites under pin-loading, which is the typical loading case for mechanical joint, was presented. Seven types of specimens with different configuration were tested to evaluate the influence of the geometry on the failure modes. The testing results stated that, with the increasing of width-to-hole diameter ratio (W/D) and edge distance-to-hole diameter ratio (E/D), the net tension and shear out failure transformed into the bearing failure respectively, while hole diameter-to-thickness ratio (D/t) hardly affect the failure mode. For a further exploration for damage mechanism of the acceptable bearing failure in engineering, damage accumulation and evolution were assessed combining numerical simulation and acoustic emission monitoring. In view of the complexity of satin woven framework, the hierarchical multiscale numerical strategy from micro-to macro-level was proposed to obtain the material mechanical performance. In order to acquire reliable prediction and consider the effects of the uncertainty sources on composite properties, the model geometry reconstruction was performed using X-ray tomography. Meanwhile, the fiber and void random distributions were determined via the Random Sequential Adsorption algorithm. The Murakami-Ohno damage theory was adopted to characterize the damage propagation. It is concluded that, the numerical prediction agreed with the testing results reasonably well, and the main damage mechanism during the bearing failure included matrix cracking, yarns pulling-out and yarns fracture matching various amplitude ranges of acoustic emission signals.