Abstract:In this paper, the fatigue life of 2D woven ceramic-matrix composites, i.e., SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate, at room and elevated temperatures has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. The Budiansky-Hutchinson-Evans shear-lag model was used to describe the microstress field of the damaged composite considering fibers failure. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. The interface shear stress and fibers strength degradation model and oxidation region propagation model have been adopted to analyze the fatigue and oxidation effects on fatigue life of the composite, which is controlled by interface frictional slip and diffusion of oxygen gas through matrix multicrackings. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface/fiber oxidation model, interface wear model and fibers statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfy the Global Load Sharing (GLS) criterion. When the broken fibers fraction approaches to the critical value, the composites fatigue fractures. The fatigue life S-N curves of 2D SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate composites at room temperature and 800, 1000 and 1200 °C in air and steam have been predicted.

Prediction of fatigue limit stress in C/SiC composites: Effect of stochastic load spectrum

Micromechanical life prediction method of fiber-reinforced ceramic-matrix composites subjected to stochastic overloading at room temperature

A stochastic theory of cumulative fatigue damage

Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

Prediction of long-term fatigue life of CFRP composite hydrogen storage vessel based on micromechanics of failure

Fast and synergetic fatigue life prediction of short fiber reinforced polymer composites from monotonic and cyclic loading behavior

Experimental investigation and multiscale simulation on the bending fatigue of 2D SiCf/SiC composites

Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air

Effect of Stochastic Loading on Tensile Damage and Fracture of Fiber-Reinforced Ceramic-Matrix Composites

Effect of Stress Ratio and Loading Inclination on the Fatigue Life of Carbon-Fiber-Reinforced Polymer Composites: Multiscale Analysis Approach

A Robust Life Prediction Model for a Range of Materials under Creep-Fatigue Interaction Loading Conditions

Experimental investigation and multiscale simulation on the bending fatigue of SiCf/SiC composite vanes

Fatigue life prediction considering individual modulus for unidirectional needled C/SiC composites under variable amplitude loading

Fatigue life prediction of metal materials under random loads based on load spectrum extrapolation

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation

Vibration fatigue life prediction method for needled C/SiC composite based on frequency response curve with low signal strength

Degradation analysis on high-cycle bending fatigue for woven SiC/SiC composites based on Wiener process model

Fuzzy fatigue life prediction of fiber-reinforced laminated composites by continuum damage mechanics

Strength and stiffness degradation modeling and fatigue life prediction of composite materials based on a unified fatigue damage model

The Effect of Random Load on Life Prediction of High-Temperature Ceramic Matrix Composites