Abstract:The quest for lightweight and functional materials poses stringent requirements on mechanical performance of porous materials. However, the contradiction between high strength and elevated porosity of porous materials severely limits their application scenarios in emerging fields. Herein, high-strength multifunctional mullite-based porous ceramic monoliths were fabricated utilizing waste fly ash hollow microspheres (FAHMs) by the protein gelling technique. Owing to their unique shell-pore structure inspired by shell-protected biomaterials, the monoliths with porosity of 54.69%–70.02% exhibited a high compressive strength (32.3–42.9 MPa) which was 2–5 times that of mullite-based porous ceramics with similar density reported elsewhere. Moreover, their pore structure and properties could be tuned by regulation of the particle size and content of the FAHMs, and the resultant monoliths demonstrated superior integrated performances for multifunctional applications, such as broadband sound insulation, efficient thermal insulation, and high-temperature fire resistance (>1300 °C). On this basis, mullite-based porous ceramic lattices (porosity 68.28%–84.79%) with a hierarchical porous structure were successfully assembled by direct ink writing (DIW), which exhibited significantly higher compressive strength (3.02–10.77 MPa) than most other ceramic lattices with comparable densities. This unique shell-pore structure can be extended to other porous materials, and our strategy paves a new way for cost-effective, scalable and green production of multifunctional materials with well-defined microstructure.

Preparation and characteristics of honeycomb mullite ceramics with controllable structure by stereolithography 3D printing and in-situ synthesis

A Comprehensive Study on Zirconia Slurry for Stereolithography-Based Additive Manufacturing

Vat photopolymerization 3D printing of thermal insulating mullite fiber-based porous ceramics

Preparation of High-Stability Ceramic Slurry with Gel Behavior for Stereolithography 3D Printing

Reinforcement effect in printing precision and sintering performance for liquid crystal display stereolithography additive manufacturing of alumina ceramics

3D printing of hollow lattice structures of ZrO2(3Y)/Al2O3 ceramics by vat photopolymerization: Process optimization, microstructure evolution and mechanical properties

High-strength, multifunctional and 3D printable mullite-based porous ceramics with a controllable shell-pore structure

Fabrication of fine and complex lattice structure Al2O3 ceramic by digital light processing 3D printing technology

3D Printing of Honeycomb Si3N4 Ceramic

Near‐net‐size Preparation of Porous Mullite Matrix Ceramics with in Situ Formed 3D Mullite Whisker Network

Fabrication of alumina ceramics with high flexural strength using stereolithography

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

Fabrication and properties of diatomite ceramics with hierarchical pores based on direct stereolithography

Formation mechanism and controlling strategy of lamellar structure in 3D printed alumina ceramics by digital light processing

Fabrication and characterization of porous mullite ceramics with ultra-low shrinkage and high porosity via sol-gel and solid state reaction methods

Low-temperature Synthesis of Highly Porous Whisker-Structured Mullite Ceramic from Kaolin

Preparation of silicon carbide ceramic slurry for stereolithography based additive manufacturing

Enhanced high-temperature dimensional accuracy by fibers in silica ceramic cores prepared through vat photopolymerization 3D printing

Preparation of high solid loading and low viscosity ceramic slurries for photopolymerization-based 3D printing

Additive Manufacturing and Characterization of Complex Al2o3 Parts Based on A Novel Stereolithography Method

Porous Mullite Ceramics with Hierarchical Pores Constructed Via Vat Photopolymerization of Multi-Phase Pickering Emulsion