Fabrication of Porous Mullite Ceramics by Freeze Drying Method Combined with Starch Consolidation

Hao LI,Yong-jun CHEN,Jian-bao LI,Li-jie LUO

DOI: https://doi.org/10.16553/j.cnki.issn1000-985x.2017.02.012

2017-01-01

Abstract:Interconnected porous mullite ceramics were fabricated by freeze-drying process combining starch consolidation,using kaolin,aluminum hydroxide as starting materials,starch as consolidator and binder and Y2O3 as sintering additive.The effects of starch content on the slurry rheological property,porosity,pore-size distribution,microstructure and mechanical strength of porous mullite ceramics were investigated.It is found that the viscosity of slurry increased significantly with the starch addition increased from 15.84vol％ to 20.59vol％,but decreased dramatically with the increase of shear rate and tended to be steady,suggesting a slight shear-thinning behavior.With the starch content increasing,the pore size of the ceramics decreased,displaying a homogeneous pore size distribution from bimodal to unimodal.Meanwhile,the porosity changed slightly and kept in the range of 61.5％-66.2％.In addition,when the starch content increased to 15.84vol％,the compressive strength of ceramics increased to the maximum values of 9.5 MPa,porosity also increased to 65.7％.However,the compressive strength tend to decease with the further increase of starch content.