Low‐temperature preparation of high‐performance porous ceramics composed of anorthite platelets
Lei Han,Liang Huang,Longhao Dong,Haijun Zhang,Yuantao Pei,Faliang Li,Quanli Jia,Shaowei Zhang
DOI: https://doi.org/10.1111/jace.17265
IF: 4.186
2020-06-26
Journal of the American Ceramic Society
Abstract:<p>Platelet‐like anorthite porous ceramics with improved mechanical strength were fabricated <i>via </i> direct gelcasting and firing at 1223‐1473 K using CaCO<sub>3</sub>, Al(OH)<sub>3</sub> and SiO<sub>2</sub> powders as the raw materials, along with H<sub>3</sub>BO<sub>3</sub> and melamine sintering/crosslinking agents. Based on DFT calculations, H<sub>3</sub>BO<sub>3</sub> promoted the formation of platelet‐like anorthite at a relatively low temperature via covering the {130} facet of anorthite and reducing the corresponding adsorption energy, which led to the preferential growth along the <i>a </i>‐ and <i>b </i>‐axes. The optimal amount of H<sub>3</sub>BO<sub>3</sub> for the anorthite platelet formation was 0.9 wt%. The porous anorthite sample with an original solid content of 22.0 wt%, after firing at 1373 K, contained 71.0% porosity and exhibited a compressive strength as high as 5.7 MPa, which were comparable or even superior to those of porous anorthite ceramics prepared previously at a much higher temperature (1573‐1723 K), indicating that the preparation strategy reported in this paper is feasible in fabricating high‐performance porous anorthite ceramic at a much milder condition. The thermal conductivity of the porous anorthite sample at 1073 K was as low as 0.266 W/(m·K), while the control sample showed a value of 0.645 W/(m·K), suggesting that the former exhibited much lower thermal conductivity value, and thus could be potentially used for thermal insulation at high temperatures.</p>
materials science, ceramics