Lei Han,Liang Huang,Longhao Dong,Haijun Zhang,Yuantao Pei,Faliang Li,Quanli Jia,Shaowei Zhang

DOI: https://doi.org/10.1111/jace.17265

IF: 4.186

2020-06-26

Journal of the American Ceramic Society

Abstract:<p>Platelet‐like anorthite porous ceramics with improved mechanical strength were fabricated <i>via </i> direct gelcasting and firing at 1223‐1473 K using CaCO₃, Al(OH)₃ and SiO₂ powders as the raw materials, along with H₃BO₃ and melamine sintering/crosslinking agents. Based on DFT calculations, H₃BO₃ promoted the formation of platelet‐like anorthite at a relatively low temperature via covering the {130} facet of anorthite and reducing the corresponding adsorption energy, which led to the preferential growth along the <i>a </i>‐ and <i>b </i>‐axes. The optimal amount of H₃BO₃ for the anorthite platelet formation was 0.9 wt%. The porous anorthite sample with an original solid content of 22.0 wt%, after firing at 1373 K, contained 71.0% porosity and exhibited a compressive strength as high as 5.7 MPa, which were comparable or even superior to those of porous anorthite ceramics prepared previously at a much higher temperature (1573‐1723 K), indicating that the preparation strategy reported in this paper is feasible in fabricating high‐performance porous anorthite ceramic at a much milder condition. The thermal conductivity of the porous anorthite sample at 1073 K was as low as 0.266 W/(m·K), while the control sample showed a value of 0.645 W/(m·K), suggesting that the former exhibited much lower thermal conductivity value, and thus could be potentially used for thermal insulation at high temperatures.</p>

materials science, ceramics