Abstract:Platelet‐like anorthite porous ceramics with improved mechanical strength were fabricated via direct gelcasting and firing at 1223‐1473 K using CaCO3, Al(OH)3 and SiO2 powders as the raw materials, along with H3BO3 and melamine sintering/crosslinking agents. Based on DFT calculations, H3BO3 promoted the formation of platelet‐like anorthite at a relatively low temperature via covering the {130} facet of anorthite and reducing the corresponding adsorption energy, which led to the preferential growth along the a ‐ and b ‐axes. The optimal amount of H3BO3 for the anorthite platelet formation was 0.9 wt%. The porous anorthite sample with an original solid content of 22.0 wt%, after firing at 1373 K, contained 71.0% porosity and exhibited a compressive strength as high as 5.7 MPa, which were comparable or even superior to those of porous anorthite ceramics prepared previously at a much higher temperature (1573‐1723 K), indicating that the preparation strategy reported in this paper is feasible in fabricating high‐performance porous anorthite ceramic at a much milder condition. The thermal conductivity of the porous anorthite sample at 1073 K was as low as 0.266 W/(m·K), while the control sample showed a value of 0.645 W/(m·K), suggesting that the former exhibited much lower thermal conductivity value, and thus could be potentially used for thermal insulation at high temperatures.

Macro/mesoporous SiOC Ceramics of Anisotropic Structure for Cryogenic Engineering

Anisotropic Porous Ceramic Material with Hierarchical Architecture for Thermal Insulation

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

In Situ Formation of the TiCN Phase in SiBCN Ceramic Aerogels Enabling Superior Thermal and Structural Stability Up to 1800 °C.

High Temperature Structure Evolution of Macroporous SiOC Ceramics Prepared by a Sol–gel Method

Hierarchically porous Al2TiO5 ceramics via freeze-gel casting

Low‐temperature preparation of high‐performance porous ceramics composed of anorthite platelets

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Preparation and Structural Evolution of SiOC Preceramic Aerogel During High-Temperature Treatment

Microstructure dependent ablation behaviour of precursor derived SiOC ceramic foam for high temperature applications

Preparation and characteristics of porous anorthite ceramics with high porosity and high‐temperature strength

Microstructure and properties of highly porous Y2SiO5 ceramics produced by a new water-based freeze casting

Zeolite ceramics with ordered microporous structure and high crystallinity prepared by cold sintering process

Hollow-grained “Voronoi foam” ceramics with high strength and thermal superinsulation up to 1400 °C

Fabrication and properties of Si2N2O ceramics for microwave sintering furnace

Enhanced Mechanical Properties of SiC/Al Composites at Cryogenic Temperatures

Microporosity evolution in polymer‐derived SiOC glasses pyrolyzed in different atmospheres

A Simple and Efficient Way to Prepare Porous Mullite Matrix Ceramics Via Directly Sintering SiO2-Al2O3 Microspheres

Effect of annealing temperature on the microstructure, dielectric, and microwave absorption performance of precursor blends derived ZrSiOCN ceramics

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Alumina Porous Ceramics Obtained by Freeze Casting: Structure and Mechanical Behaviour under Compression