Abstract:TiF3-doped NaH/Al mixture was hydrogenated into Na3AlH6 and NaAlH4 complex hydrides by reactive ball-milling at room temperature through the optimization of milling duration and hydrogen pressure. The analysis of the preparation of NaAlH4 samples during reactive ball-milling process has been performed by XRD and TG/DSC. It has been found that Na3AlH6 was formed under 0.5 MPa hydrogen pressure and 30 h milling duration, while NaAlH4 was formed under 0.8 MPa hydrogen pressure and 45 h milling duration. The process of preparing NaAlH4 by ball-milling was found accomplished via two reaction steps, namely: (1) NaH + Al + H-2 Na3AlH6 and (2) Na3AlH6 + Al + H-2 -> NaAlH4. As the hydrogen pressure and milling duration increase, the synthetic yield of NaAlH4 and its corresponding dehydriding capacity are both increased. With increased hydrogen pressure (0.8-3 MPa) and milling duration (45-60 h), the cell volume of Na3AlH6 decreases while that of NaAlH4 increases gradually. The abundance of Na3AlH6 phase decreases from 57.76 (x = 0.8, y = 45) to 8.69 wt.% (x = 3, y = 60), and the abundance of NaAlH4 phase increases from 20.63 (x = 0.8, y = 45) to 86.50 wt.% (x = 3, y = 60). All the samples prepared in this way have fairly good activation behavior and fast hydriding/dehydriding reaction kinetics, which are capable of absorbing 4.26 wt.% hydrogen at 120 degrees C and desorbing 4.12 wt.% hydrogen at 150 degrees C, respectively. The improvement of hydriding/dehydriding properties is ascribed to the favorable microstructure and ultrafine particle features of nanosized NaAlH4 formed during ball-milling at the optimum synthetic condition. (C) 2010 Professor T. Nejat Veziroglu. Published by Elsevier Ltd. All rights reserved.

An x-ray photoemission electron microscopy study of the formation of Ti-Al phases in 4 mol% TiCl3 catalyzed NaAlH4 during high energy ball milling

The Hydrogen Storage Properties and Microstructure of Ti-Doped Sodium Aluminum Hydride Prepared by Ball-Milling

High-energy ball milling of Al2O3–TiO2 powders

Formation of Nanocrystalline Fcc Phase by Mechanically Driven Crystallization

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Amorphization in the AlC System by Mechanical Alloying

Preparation of ti-al based nanophase composite powder by mechanical alloying

Achieving Both High Hydrogen Capacity and Low Decomposition Temperature of the Metastable AlH3 by Proper Ball Milling with TiB2

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Preparation and hydrogen storage characteristics of Ti-NaAlH4 complex hydride

Preparations and Electrochemical Properties of Amorphous Ti-Al Alloys

Effect of ball-milling on the phase structure and hydrogen storage properties of Ti0.9Zr0.1Mn1.5 alloy

TEM characterization of pure and transition metal enhanced NaAlH4

Metastable state transformations of Al3Ti-base alloys during mechanical milling and subsequent annealing

Deformation-induced Reactions of ZnO and TiO2

Ti2SnC MAX Phase Directly Synthesized by High-Temperature Ball Milling

Synthesis and characterization of nanocrystalline Ti(1-x)Al(x)N by reactive magnetron sputtering

Synthesis and Hydriding/dehydriding Properties of Nanosized Sodium Alanates Prepared by Reactive Ball-Milling

Mechanical alloying and thermal analysis of Ta–Ti alloys

Phase Transformation and Morphology Evolution of Ti50Cu25Ni20Sn5 during Mechanical Milling