Abstract:The synergistic effect of metallic Ti and Zr as co-dopants on the reversible hydrogen storage properties of NaAlH4 was investigated systematically. Metallic Ti and Zr powders were used directly and separately as dopants, as well as used as co-dopants together in the preparation of NaAlH4 by hydrogenation of ball-milled mixtures of NaH/Al. The hydriding/dehydriding properties of the composites were then investigated. It was found that the addition of Ti and Zr powders together as co-dopants on hydriding/dehydriding properties is superior to doping with Ti or Zr alone. The highest reversible hydrogen capacity of the hydride doped with Ti and Zr together as co-dopants is 4.34wt% at 160∘C. The hydriding rate increases with the hydriding pressure increasing from 7.5 to 11.5MPa. The dehydriding kinetics is improved with the dehydriding temperature increasing from 90 to 130∘C, and the dehydriding rate of the composite doped with Ti and Zr as co-dopants is 1.6 and 2.0 times that of the sample doped with Ti and Zr alone at 130∘C. Microstructure analysis reveals that the improvement of the hydriding/dehydriding properties of NaH/Al (NaAlH4) can be partially ascribed to the in situ interaction of active titanium-hydride and zirconium-hydrides formed in the ball-milling process and subsequently acted as the catalytic active sites on the surface of hydride matrix. The effect of lattice expansion on enthalpy change indicates that the further improved dehydriding property of the composite can also be attributed to a favorable thermodynamic modification of the bulk composite hydride co-doped with Ti–Zr powders. In a word, the synergistic effect on the improvement of hydriding/dehydriding properties by introducing the addition of Ti–Zr together as co-dopants can be ascribed to both the “superficial catalytic process” and the “favorable thermodynamic modification” of the composite.

Preparation and hydrogen storage characteristics of Ti-NaAlH4 complex hydride

The Hydrogen Storage Properties and Microstructure of Ti-Doped Sodium Aluminum Hydride Prepared by Ball-Milling

Sodium Alanate In-Situ Doped with Ti2C MXene with Enhanced Hydrogen Storage Properties

Remarkable Hydrogen Absorption/desorption Behaviors and Mechanism of Sodium Alanates In-Situ Doped with Ti-based 2D MXene

Influence of Temperature and Hydrogen Pressure on the Hydriding/dehydriding Behavior of Ti-doped Sodium Aluminum Hydride

Dehydriding Properties of Ti Or/and Zr-doped Sodium Aluminum Hydride Prepared by Ball-Milling

Hydrogen storage properties of Ti/TiF3-doping LiAlH4/LiNH2 composites

Reversible Hydrogen Storage Behaviors and Microstructure of TiC-doped Sodium Aluminum Hydride

Reversible Hydrogen Storage Properties and Favorable Co-Doping Mechanism of the Metallic Ti and Zr Co-Doped Sodium Aluminum Hydride

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Catalytic Mechanism of New Tic-Doped Sodium Alanate for Hydrogen Storage

Dehydriding properties of γ-AlH3

Microstructure And Hydrogen Storage Properties Of La1.8ca0.2mg14ni3 + X% Ti Composites

Directed Stabilization by Air-Milling and Catalyzed Decomposition by Layered Titanium Carbide Toward Low-Temperature and High-Capacity Hydrogen Storage of Aluminum Hydride

Mixtures Doped with Titanium Based Catalysts

Direct Synthesis of Nanocrystalline Naalh4 Complex Hydride for Hydrogen Storage

Synthesis and Hydriding/dehydriding Properties of Nanosized Sodium Alanates Prepared by Reactive Ball-Milling

Investigation on reversible hydrogen storage properties of Li3AlH6/2LiNH2 composite

Influence of Ti-Zr Catalysts on Reversible Hydrogen Storage Characteristics of NaH/Al Composite

Influence of TiC Catalyst on Absorption/desorption Behaviors and Microstructures of Sodium Aluminum Hydride

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys