Making high-performance MoAlB ceramics by hot pressing combustion-synthesized powders

Yuehai Song,Enliang Zhang,Yehong Cheng,Yongting Zheng,Dongyue Sun,Xiangming Li,Wanjun Yu

DOI: https://doi.org/10.1016/j.ceramint.2023.07.253

IF: 5.532

2023-07-01

Ceramics International

Abstract:It is one of the most concerning issues to achieve high purity, low cost and excellent performance in MAB phases. Herein, the MoAlB powders were synthesized by an ultra-fast combustion synthesis (CS). The reaction mechanism was analyzed by changing components of raw materials. The high-purity MoAlB powders were successfully obtained with the mole ratio of Mo, Al and B of 1:1.3:1. After hot-pressing sintering, the powders were densified and formed compact MoAlB ceramics. Together with phase composition, microstructure, mechanical properties, toughening mechanisms, and oxidation resistance properties were collaboratively outlined. The flexural strength, fracture toughness and Vickers hardness of MoAlB ceramic hot-pressed at 1300 °C reach up to 640 ± 22.37 MPa, 6.82 ± 0.64 MPa m1/2 and 13.82 ± 0.41 GPa, which far surpass these values of ternary layered compounds prepared by other methods. The oxidation resistance was investigated up to 1200 °C, where a passivating Al2O3 layer inhibited further oxidation even when treatment sample for 12 h. This work provides a guidance to industrially produce MAB phases with high performance.

materials science, ceramics