Abstract:Siliceous mesostructured cellular foams (MCF) impregnated with polyethylenimine (PEI) of various molecular weights and structures were evaluated as CO2 adsorbents. The MCF solid support consisted of a well-defined interconnected three-dimensional mesoporous structure with large cell diameter of 30.3 nm and large window diameter of 11.3 nm, filled with polyethylenimine up to 70 weight percent or about 22.3% nitrogen atom by weight of the adsorbents. While other mesoporous solid supports lost their porosity after PEI impregnation, our MCF solid support maintained its pore volume over the range of 1.12 to 1.64 cm(3) g(-1). The importance of the porosity of PEI-impregnated MCF adsorbents for high capacity CO2 adsorbents was demonstrated. The highest CO2 sorption capacity (180.6 mg-CO2/g-adsorbent or 393.6 mg-CO2/g-PEI at 75 degrees C) was obtained for silica supports loaded with 50 weight percent branched PEI with average molecular weight of 600 g mol(-1). Under dry atmospheric CO2 gas, this adsorbent reached the theoretical CO2 capacity of 0.50 mole-CO2 per mole-nitrogen within less than about 8 min, making this adsorbent one of the most effective CO2 adsorbents reported. Repeated multiple sorption cycles demonstrated good stability of this adsorbent for CO2 capture. The initial sorption kinetics determined the overall CO2 sorption capacity, which was limited by the formation of a carbamate layer as a result of the CO2-PEI complexation that due to inhibition of CO2 diffusion; the kinetics of "ionic" gelation of the impregnated PEI by CO2 controlled the overall performance of the CO2 adsorbents. At 75 degrees C, the operating temperature favored the molecular mobility of PEI and unrestricted diffusion of CO2 to allow the theoretical CO2 capacity of the PEI to be attained. Lower temperatures limited the mobilities of PEI and CO2 and the kinetics of "ionic" gel formation dominated, causing a lowered overall performance of the CO2 adsorbents. Overall, this study points to the importance of interconnected porous channel networks to optimize the performance of PEI-impregnated mesoporous silica particles.

Polymer-Grafted Porous Silica Nanoparticles with Enhanced CO 2 Permeability and Mechanical Performance

Polymer-Grafted Porous Silica Nanoparticles With Enhanced Co2 Permeability And Mechanical Performance

Nanostructured Poly(l-Lactic Acid)-Poly(ethylene Glycol)-Poly(l-lactic Acid) Triblock Copolymers and Their CO2/O-2 Permselectivity

CO2 Facilitated Transport Through an Acrylamide and Maleic Anhydride Copolymer Membrane

Synthesis of Poly(ionic Liquid)s- block -poly(methyl Methacrylate) Copolymer-Grafted Silica Particle Brushes with Enhanced CO 2 Permeability and Mechanical Performance

Synthesis of Poly(ionic Liquid)s-<i>block</i>-poly(methyl Methacrylate) Copolymer-Grafted Silica Particle Brushes with Enhanced CO<sub>2</sub> Permeability and Mechanical Performance

Preparation and characterization of crystalline poly(L‐lactic acid)/silica nanocomposite films with high ductility and gas barrier properties

CO2 Adsorption by Polyamine-Based Protic Ionic Liquid-Functionalized Mesoporous Silica: Regenerability and Influence of Flue Gas Contaminants

Mesoporous Silica-Reinforced Polymer Nanocomposites

Rational design of silicas with meso-macroporosity as supports for high-performance solid amine CO2 adsorbents

Periodic Mesoporous Organosilica Nanocubes with Ultrahigh Surface Areas for Efficient CO2 Adsorption

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

PDMS‐silica composite gas separation membranes by direct ink writing

Polymethacrylate-Silica Hybrid Nanoporous Materials: A Bridge Between Inorganic and Polymeric Molecular Sieves

Polyethylenimine-Impregnated Siliceous Mesocellular Foam Particles As High Capacity Co2 Adsorbents

Improving gas permeation performance of PDMS by incorporating hollow polyimide nanoparticles with microporous shells and preparing defect-free composite membranes for gas separation

Nanocomposite Membranes for CO2 Separations: Silica/Brominated Poly(phenylene Oxide)

Facile Synthesis of Poly(methyl methacrylate) Silica Nanocomposite Monolith by In Situ Free Radical Polymerization of Methyl Methacrylate in the Presence of Functionalized Silica Nanoparticles

Exploring the confinement of polymer nanolayers into ordered mesoporous silica using advanced gas physisorption

Insight into the aminosilane functionalized-montmorillonite/Pebax mixed matrix membranes with selectively fast gas transport channels for CO 2 permeation

Controlling Foam Morphology of Poly(methyl methacrylate) via Surface Chemistry and Concentration of Silica Nanoparticles and Supercritical Carbon Dioxide Process Parameters