Abstract:Siliceous mesostructured cellular foams (MCF) impregnated with polyethylenimine (PEI) of various molecular weights and structures were evaluated as CO2 adsorbents. The MCF solid support consisted of a well-defined interconnected three-dimensional mesoporous structure with large cell diameter of 30.3 nm and large window diameter of 11.3 nm, filled with polyethylenimine up to 70 weight percent or about 22.3% nitrogen atom by weight of the adsorbents. While other mesoporous solid supports lost their porosity after PEI impregnation, our MCF solid support maintained its pore volume over the range of 1.12 to 1.64 cm(3) g(-1). The importance of the porosity of PEI-impregnated MCF adsorbents for high capacity CO2 adsorbents was demonstrated. The highest CO2 sorption capacity (180.6 mg-CO2/g-adsorbent or 393.6 mg-CO2/g-PEI at 75 degrees C) was obtained for silica supports loaded with 50 weight percent branched PEI with average molecular weight of 600 g mol(-1). Under dry atmospheric CO2 gas, this adsorbent reached the theoretical CO2 capacity of 0.50 mole-CO2 per mole-nitrogen within less than about 8 min, making this adsorbent one of the most effective CO2 adsorbents reported. Repeated multiple sorption cycles demonstrated good stability of this adsorbent for CO2 capture. The initial sorption kinetics determined the overall CO2 sorption capacity, which was limited by the formation of a carbamate layer as a result of the CO2-PEI complexation that due to inhibition of CO2 diffusion; the kinetics of "ionic" gelation of the impregnated PEI by CO2 controlled the overall performance of the CO2 adsorbents. At 75 degrees C, the operating temperature favored the molecular mobility of PEI and unrestricted diffusion of CO2 to allow the theoretical CO2 capacity of the PEI to be attained. Lower temperatures limited the mobilities of PEI and CO2 and the kinetics of "ionic" gel formation dominated, causing a lowered overall performance of the CO2 adsorbents. Overall, this study points to the importance of interconnected porous channel networks to optimize the performance of PEI-impregnated mesoporous silica particles.

Periodic Mesoporous Organosilica Nanocubes with Ultrahigh Surface Areas for Efficient CO2 Adsorption

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Defect-controlled confined growth of nano-MOFs to prepare materials with hierarchical micro/mesoporous structures for efficient CO 2 capture

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Structurally Designed Synthesis of Mechanically Stable Poly(benzoxazine-co-resol)-Based Porous Carbon Monoliths and Their Application As High-Performance CO2 Capture Sorbents

Preparation of Hydrophobic Hierarchical Pore Carbon–silica Composite and Its Adsorption Performance Toward Volatile Organic Compounds

Synthesis and CO2 adsorption property of amino-functionalized silica nanospheres with centrosymmetric radial mesopores

Highly ordered periodic mesoporous organosilica nanoparticles with controllable pore structures

Amine functionalized mesocellular silica foam as highly efficient sorbents for CO2 capture

Adsorption Capacity of Carbon Dioxide on Amine Modified Mesoporous Materials with Larger Pore Sizes

Ultrahigh–surface area covalent organic frameworks for methane adsorption

Hierarchically Porous Structured Adsorbents with Ultrahigh Metal-Organic Framework Loading for CO2 Capture

Investigation of adsorption/desorption performance by aminopropyltriethoxysilane grafted onto different mesoporous silica for post-combustion CO2 capture

Synthesis and Electrospraying of Nanoscale MOF (Metal Organic Framework) for High-Performance CO2 Adsorption Membrane

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

An Unusual Example of Morphology Controlled Periodic Mesoporous Organosilica Single Crystals

Polyethylenimine-Impregnated Siliceous Mesocellular Foam Particles As High Capacity Co2 Adsorbents

High CO2 adsorption on amine-functionalized improved macro-/mesoporous multimodal pore silica

Facile Large-Scale Synthesis of Macroscopic 3D Porous Graphene-Like Carbon Nanosheets Architecture for Efficient CO2 Adsorption

Rational design of silicas with meso-macroporosity as supports for high-performance solid amine CO2 adsorbents