Ni-Cr textured substrates with reduced ferromagnetism for coated conductor applications

J. R. Thompson,A. Goyal,D. K. Christen,D. M. Kroeger

DOI: https://doi.org/10.1016/S0921-4534%2801%2900937-6

2001-04-13

Abstract:A series of biaxially textured Ni(1-x)Cr(x) materials, with compositions x = 0, 7, 9, 11, and 13 at % Cr, have been studied for use as substrate materials in coated conductor applications with high temperature superconductors. The magnetic properties were investigated, including the hysteretic loss in a Ni-7 at % Cr sample that was controllably deformed; for comparison, the loss was also measured in a similarly deformed pure Ni substrate. Complementary X-ray diffraction studies show that thermo-mechanical processing produces nearly complete {100}<100> cube texturing, as desired for applications.