Abstract:In this present work, a novel electrostatic self-assembly method was invented to produce AlSi10Mg powders homogeneously decorated with TiC nanoparticles. The TiC/AlSi10Mg alloy with homogenous, crack-free, equiaxed and super fine-grained were produced using selective laser melting (SLM). The in-situ formation of D022-Al3Ti created by TiC and Al matrix during SLM was revealed at the first time and both TiC and D022-Al3Ti nanoparticles were extremely effective inoculant for an SLMed AlSi10Mg alloy. Therefore, the SLMed TiC/AlSi10Mg alloy exhibited a high tensile strength (ultimate tensile strength ~ 456 MPa, yield strength ~338 MPa) and high microhardness (131 HV0.05), which were higher than the SLMed AlSi10Mg alloy (ultimate tensile strength ~437 MPa, yield strength ~254 MPa and microhardness ~113 HV0.05). This study can be regarded as a guidance in the fabrication of metal matrix nanocomposites using for SLM.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the microstructure and mechanical properties of AlSi10Mg alloy through the uniform dispersion of nano - TiC particles during the Selective Laser Melting (SLM) process. Specifically, the authors have invented a new electrostatic self - assembly method for preparing AlSi10Mg powder with uniformly dispersed TiC nanoparticles. This method can prevent the agglomeration of TiC nanoparticles and maintain the sphericity of AlSi10Mg powder. By processing this composite powder with SLM technology, the researchers found that TiC nanoparticles can be used as effective heterogeneous nucleating agents to promote the Columnar - to - Equiaxed Transition (CET), thereby eliminating the anisotropy of the material and improving its mechanical properties. The key achievements of the paper include: 1. **Improvement of microstructure**: By adding TiC nanoparticles, the microstructure of SLMed TiC/AlSi10Mg alloy has changed from coarse columnar crystals to ultrafine equiaxed crystals, with an average grain size of about 1 μm. In contrast, the SLMed AlSi10Mg alloy without added TiC is mainly composed of coarse columnar crystals, which grow along the building direction, resulting in the anisotropy of the material. 2. **Improvement of mechanical properties**: The Ultimate Tensile Strength (UTS) of SLMed TiC/AlSi10Mg alloy reaches about 456 MPa, the Yield Strength (YS) reaches about 338 MPa, and the Microhardness (HV) is 131 HV0.05, all higher than those of SLMed AlSi10Mg alloy without added TiC (UTS is about 437 MPa, YS is about 254 MPa, and microhardness is 113 HV0.05). In addition, the paper also explores the in - situ formation mechanism of D022 - Al3Ti phase. During the SLM process, TiC reacts with the Al matrix to generate D022 - Al3Ti phase, and these phases, as heterogeneous nucleating agents, further promote the occurrence of CET, thereby improving the mechanical properties of the material. In conclusion, this research provides a new method and theoretical basis for preparing high - performance metal - based nanocomposites through SLM technology.

In situ formation of D022-Al3Ti during selective laser melting of nano-TiC/AlSi10Mg alloy prepared by electrostatic self-assembly

Selective Laser Melting of Nano-Tib2 Decorated Alsi10mg Alloy with High Fracture Strength and Ductility

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting

Microstructure and Mechanical Behavior of TiCN Reinforced AlSi10Mg Composite Fabricated by Selective Laser Melting

Interfacial structures and strengthening mechanisms of in situ synthesized TiC reinforced Ti6Al4V composites by selective laser melting

Mechanical Properties of In-Situ Synthesis of Ti-Ti3Al Metal Composite Prepared by Selective Laser Melting

High-strength and thermally stable TiB2-modified Al–Mn–Mg–Er–Zr alloy fabricated via selective laser melting

Selective Laser Melting Enabled Additive Manufacturing of Ti-22Al-25Nb Intermetallic: Excellent Combination of Strength and Ductility, and Unique Microstructural Features Associated

Effect of nano-TiB2 particles on the anisotropy in an AlSi10Mg alloy processed by selective laser melting

Microstructure, heat treatment and mechanical properties of TiB2/Al–7Si–Cu–Mg alloy fabricated by selective laser melting

Selective Laser Melting of High-Strength TiB2/AlMgScZr Composites: Microstructure, Tensile Deformation Behavior, and Mechanical Properties

Inoculation treatment of an additively manufactured 2024 aluminium alloy with titanium nanoparticles

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Effect of In-Situ TiB2 Particles on Microstructure and Mechanical Properties of Al–Fe–Ni Manufactured by Selective Laser Melting

A novel crack-free Ti-modified Al-Cu-Mg alloy designed for selective laser melting

Microstructure evolution and mechanical properties of selective laser melting fabricated hybrid particle reinforced AlSi10Mg composites

Preparation of Ti2AlC through in-situ selective laser forming and reaction sintering

In-situ synthesis of Ti<sub>5</sub>Si<sub>3</sub>-reinforced titanium matrix nanocomposite by selective laser melting: Quasi-continuous reinforcement network and enhanced mechanical performance

Microstructure and inclusion of Ti–6Al–4V fabricated by selective laser melting

Nano-SiC whisker-reinforced Ti6Al4V matrix composites manufactured by selective laser melting: fine equiaxed grain formation mechanism and mechanical properties