Abstract:In order to investigate the effect of TiB2 contents on the microstructure and wear resistance of titanium matrix composites, commercial pure Ti (CP-Ti) powders with 0–7.5 wt.% TiB2 particles were melted by selective laser melting (SLM) to produce the in-situ Ti-TiB composites. When the TiB2 content increases from 2.5 wt.% to 7.5 wt.%, the microstructures of the Ti-TiB composites undergo a transition from the single phase of α′-Ti to the mixed phases of α′-Ti, TiB and TiB2, and the acicular α′-Ti is refined significantly from 1.03 ± 0.24 μm to 0.36 ± 0.05 μm, showing that increasing the TiB2 content induces the formation of TiB and refines the microstructure. Moreover, large TiB2 particles are not melted completely and they react with the Ti matrix liquid to form a TiB layer around the Ti matrix during SLM. However, small TiB2 particles are completely dissolved into the Ti matrix liquid so that the eutectic TiB grains are precipitated at the boundaries of the Ti matrix after in-situ reaction of TiB2 with Ti. The formation of α′ martensite in the titanium matrix and the addition of TiB2 can induce the fine grain strengthening, the dispersion strengthening, the solid solution strengthening in the SLM-produced composites. The results indicate that the microhardness of the composites increases from 258 ± 10.3 HV0.2 to 435 ± 14.7 HV0.2. The wear process of the SLM-produced CP-Ti and TiB2 reinforced Ti matrix composites is accompanied by adhesion wear, abrasive wear and oxidation wear. As a result, when the TiB2 content increases to 7.5%, the wear resistance of the composites increases by 32.6% compared with that of the CP-Ti. These improvements are mainly due to strengthening and hardening effects induced by TiB2 particles and refinement of Ti matrix. This study provides some basis for developing wear-resistant and high-strength titanium alloys.

Selective laser melting of TiB2/AlSi10Mg composite: Processability, microstructure and fracture behavior

Microstructure, Mechanical Properties and Fracture Behavior of Micron-Sized TiB2/AlZnMgCu(Sc,Zr) Composites Fabricated by Selective Laser Melting

From gradient to homogenous: thermal behavior-induced microstructure evolution and mechanical properties of selective laser-melted TiB2p/2024Al composite

Microstructure evolution and mechanical properties of selective laser melting fabricated hybrid particle reinforced AlSi10Mg composites

Microstructure and mechanical properties of an in-situ TiB2 particle reinforced AlSi10Mg composite additive manufactured by selective electron beam melting

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting

Microstructure and mechanical properties of TiB 2 /Al-5Cu composites fabricated by multi-material laser powder bed fusion

Achieving near equiaxed α-Ti grains and significantly improved plasticity via heat treatment of TiB reinforced titanium matrix composite manufactured by selective laser melting

Mechanical Properties of In-Situ Synthesis of Ti-Ti3Al Metal Composite Prepared by Selective Laser Melting

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

High-strength and thermally stable TiB2-modified Al–Mn–Mg–Er–Zr alloy fabricated via selective laser melting

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

Interfacial structures and strengthening mechanisms of in situ synthesized TiC reinforced Ti6Al4V composites by selective laser melting

Novel selective laser melting processed in-situ TiC particle-reinforced Ni matrix composite with excellent processability and mechanical properties

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw

High strength and ductility of titanium matrix composites by nanoscale design in selective laser melting

Refined microstructure and enhanced wear resistance of titanium matrix composites produced by selective laser melting

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Microstructure evolution and mechanical properties of Al-Al2O3 composites fabricated by selective laser melting

Effect of laser additive manufacturing on the microstructure and mechanical properties of TiB2 reinforced Al-Cu matrix composite