Abstract:The interaction between corrosion and wear of U68CuCr rail steel was investigated. The samples were alternately subjected to the neutral salt spray tests with different corrosion periods (6, 24 and 48 hours) and rolling friction wear test for 4 hours. The corrosion and wear rates after the corrosion test and wear test were measured, respectively. The surface morphologies of the rail samples after the corrosion test and wear test, and the subsurface morphologies of the rail samples after the last test were observed. The results show that compared to the samples without corrosion, the damage degree of the corroded samples after wear tests became severer, and the wear mass loss and wear rate increased with the number of corrosion-wear cycle. In addition, rolling contact fatigue cracks initiated and propagated at a high angle and the structure of sample surface became unstable after corrosion, leading to easy spalling during the following wear tests compared to the only wear tests without corrosion. Moreover, the plastic deformation layer was destroyed by corrosion and the area of wear pits increased after the interaction test. Therefore, wear was accelerated by corrosion, and the longer is the corrosion period, the more severe is the wear degree. Additionally, regarding to the effect of wear on corrosion, corrosion was accelerated by wear. This is attributed to the facts that the wear pits and delamination on the worn samples provided favorable locations for the deposition of the salt spray solution during the corrosion, and (2) the subsurface and matrix were corroded along rolling contact fatigue cracks to increase the corrosion rate during the corrosion test after wear. This work provides a foundation to the further investigation on the interaction between corrosion and wear of steels.

Localized Corrosion Induced by MnS Inclusions in U71Mn Rail Steels

Insight into the Triggering Effect of (al, Mg, Ca, Mn)-oxy-sulfide Inclusions on Localized Corrosion of Weathering Steel

Corrosion performance of a corrosion-resistant rail steel in the simulated subsea tunnel environment

A thermodynamic assessment of precipitation, growth, and control of MnS inclusion in U75V heavy rail steel

Microstructural Evolution and Micro-Corrosion Behaviour of Flash-Welded U71Mn Joints as a Function of Post-Weld Heat Treatment

Localized corrosion of 304 stainless steel triggered by embedded MnS

Experimental investigation on corrosion fatigue crack initiation and growth of heat-treated U75V rail steel

Effect of normalizing treatments on microstructure and electrochemical corrosion properties of U75V-welded joints in an acidic environment

Localized Corrosion of Stainless Steel Triggered by Typical Inclusions in NaCl Solution: Oxy-Sulfide and MnS

In Situ Observation on the Heterogeneous Nucleation of MnS in Heavy Rail Steels with Varied Aluminum Content

Effects of Ti and Cu Addition on Inclusion Modification and Corrosion Behavior in Simulated Coarse-Grained Heat-Affected Zone of Low-Alloy Steels

Unraveling the effect of sulfide-oxide complex inclusions on the localized corrosion mechanism for carbon steel

The Effect of La, Ce Rare‐Earth Elements on the MnS Inclusion Precipitation and Distribution in U75V Heavy‐Rail Steel

Localized Corrosion Induced by Nonmetallic Inclusions in Rebar HRB400E Alloyed with Rare Earth

Non-uniform Corrosion of Steel in Mortar Induced by Impressed Current Method: an Experimental and Numerical Investigation

Improving wear and corrosion resistance of U71Mn rail steel subjected to laser in-situ fabrication of Fe based Cr‚ÄďV coatings

Towards a better understanding of localised corrosion induced by typical non-metallic inclusions in low-alloy steels

Investigation on the interaction between corrosion and wear of U68CuCr rail steel with different corrosion periods

Effect of Normalising Process on the Corrosion Behaviour of U75V Rail Flash Butt Welded Joints in a Marine Environment

Corrosion Behavior of Multiphase Bainitic Rail Steels

Localized corrosion of thermally aged Cu-containing Ni-13Cr-10Fe alloys: The role of Cu enrichment induced grain boundary sensitization