Abstract:Nb-microalloyed steels are widely used in construction engineering fields due to their excellent mechanical properties, but they face serious corrosion problems in service environments. Pitting corrosion is the severest form of corrosion, and the types of inclusions are the leading cause to induce pitting corrosion. A new strategy is proposed to enhance the corrosion resistance of steels by achieving a beneficial transformation of inclusions with Ce treatment. In this paper, two types of Nb-microalloyed steels (0% Ce and 0.0058% Ce steel) were prepared to study the modification effect on inclusions in industrial production. The spherical CaS•C12A7 inclusions were modified to smaller ellipsoidal Ce2O2S inclusions, and the proportion of inclusions (0-2 μm) increased significantly from 27 to 66%, while large inclusions (>6 μm) disappeared. A kinetic model of inclusion evolution was established. The results of electrochemical tests indicated that the corrosion potential was positively shifted, and the corrosion current was reduced after Ce treatment. Additionally, the number of defects in the passivation film was decreased, and the corrosion resistance of the steel was significantly improved. The addition of Ce changed the types of inclusions and reduced the number of pitting nucleation points, which led to a remarkable reduction in the number and size of pitting pits. The mechanism of pitting corrosion induced by different types of inclusions was further investigated, and a pitting corrosion model was modeled based on the immersion experiments. Research results provide theoretical support for enhancing the corrosion resistance of steel.

Localized Corrosion Induced by Nonmetallic Inclusions in Rebar HRB400E Alloyed with Rare Earth

Effects of Modified Inclusions and Precipitates Alloyed by Rare Earth Element on Corrosion and Impact Properties in Low Alloy Steel

Towards a better understanding of localised corrosion induced by typical non-metallic inclusions in low-alloy steels

Insight into the Triggering Effect of (al, Mg, Ca, Mn)-oxy-sulfide Inclusions on Localized Corrosion of Weathering Steel

Effect of Ce on structural evolution and corrosion resistance of HRB500E rebar corrosion layer

Effect of Solution and Precipitation of Nb on Microstructure and Strengthening Mechanism of High-Strength Anti-seismic Rebar

Effect of cooling rate and Nb synergistic strengthening on microstructure and mechanical properties of high-strength rebar

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Effect of Nb contents on the passivation behavior of high-strength anti-seismic rebar in concrete environments

The Effect of La, Ce Rare‐Earth Elements on the MnS Inclusion Precipitation and Distribution in U75V Heavy‐Rail Steel

Electrochemical Impedance Spectroscopy Characteristics of Corrosion Behavior of Rebar in Concrete

Microstructure and deformation behavior of a novel steel rebar: Effect of the heterogeneous microstructure of soft ferrite and Hard bainite

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Corrosion characteristics of rebar and its effects on concrete strength under multi-factors condition

Effect of Cerium on Inclusion Evolution and Pitting Corrosion of Nb-Microalloyed Steel.

Local Corrosion Behaviors in the Coarse-Grained Heat-Affected Zone in a Newly Developed Zr-Ti-Al-RE Deoxidized High-Strength Low-Alloy Steel

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

Investigation of Crevice Corrosion Behavior of HRB355 Steel in 3.5% NaCl solution using Coupled multi-electrode arrays

Electrochemical corrosion behavior of rebar in simulated pore solution

Research on Pitting Corrosion of Micro-alloyed High Strength Steel Bars

Synergistic Effect of Microalloying Elements on the Corrosion Behavior of an Industrially Produced Low-Carbon Steel