In Situ Observation on the Heterogeneous Nucleation of MnS in Heavy Rail Steels with Varied Aluminum Content

Tanhua Zhu,Lifeng Zhang,Peishu Song,Yaoqiang Li

DOI: https://doi.org/10.1002/srin.202200684

IF: 2.1258

2022-12-08

steel research international

Abstract:In situ observation, scanning electron microscope/energy‐dispersive spectrometer detection, and lattice disregistry calculation are combined to investigate the evolution mechanism of inclusions in heavy rail steels with varied aluminum contents from SiO2–Al2O3–MnO to SiO2–Al2O3–MnO–MnS at 1323 K and 1393 K. The precipitation of MnS inclusions on SiO2–Al2O3–MnO inclusions in the steel occurs when the Al2O3 content in identical oxide inclusions is 30% at 1393 K and 30%, 40%, and 59% at 1323 K. The MnS outer layer shows visible precipitation from 3 min after heating at experimental temperature. The area fraction of MnS phase in SiO2–Al2O3–MnO–MnS inclusions with varied Al2O3 content at 1323 K decreases in the following order: SiO2–Al2O3 (30%)–MnO > SiO2–Al2O3 (40%) –MnO > SiO2–Al2O3 (59%)–MnO. The precipitation of MnS is prone to occur on the Al2O3‐less region of the SiO2–Al2O3–MnO inclusion. The solubility of Mn and S decreases with decreasing temperature. Lower heating temperature and lower Al2O3 content in SiO2–Al2O3–MnO oxide cores are profitable to the heterogeneous nucleation of MnS due to lower disregistry between MnS with the SiO2–Al2O3–MnO inclusion.

Materials Science