Precipitation Behaviors of AlN Inclusion in High-Al Steel

Yuhang Guo,Lei Cao,Guocheng Wang,Chunwei Liu

DOI: https://doi.org/10.1007/s11663-022-02688-y

2023-01-14

Metallurgical Transactions B (Process Metallurgy)

Abstract:High-Al steel was prepared under laboratory conditions. The single-particle AlN and multi-particle aggregated AlN, AlON, AlN–MnS, and Al 2 O 3 –AlN–MnS inclusions were observed by FESEM-EDS. The single-particle AlN inclusions are mainly in the form of blocks and strips, with their size mainly concentrated in the range of 1 to 5  μ m. The aggregated AlN inclusions are polygonal, toroidal, and irregular in shape and their size mainly concentrated in the range of 1 to 13  μ m. The size of AlN–MnS and Al 2 O 3 –AlN–MnS inclusions is less than 15  μ m. Thermodynamic calculation shows that AlN inclusion precipitates in the two-phase region. Growth kinetics showed that the size of AlN inclusions at the end of solidification ranged from 1 to 7  μ m, which is consistent with the observed size of single-particle AlN inclusions. Lattice mismatch indicates that AlN can be as an effective site for MnS nucleation. The equilibrium constant of AlON inclusions is constructed. Furthermore, the mass percentage changes of inclusions during solidification were predicted based on the microsegregation model combined with the FactSage software.