Abstract:Three different nitrogenous interlayers including 1,4‐bis(2‐hydroxyethyl) piperazine, polyethylenimine ethoxylated, and polyethylenimine are studied to modify indium tin oxide (ITO) source/drain electrodes. Verified by first‐principle calculations and element analysis, the protonated amines are responsible for the decrease of ITO surface work function. N‐type organic thin film transistors with maximum field‐effect mobility of 1.95 cm2 V−1 s−1 are achieved. The commercialization of organic thin film transistors (OTFTs) is partly hindered by the high cost and stubborn work function (WF) of common Au source/drain (S/D) electrodes. In this work, indium tin oxide (ITO) S/D electrodes modified with three different nitrogenous interlayers including 1,4‐bis(2‐hydroxyethyl) piperazine (HEP), polyethylenimine ethoxylated (PEIE), and branched polyethylenimine (PEI) are adopted to fabricate n‐type OTFTs. The WF of bare ITO is 4.7 eV, whereas ITO modified with nitrogenous interlayers exhibits WFs ranging from 4.1 to 3.6 eV. By the first‐principle calculation and element analysis, the protonated amines are critical for the reduction of ITO surface WF. Besides, the interlayers with higher nitrogen contents are more likely to improve the wettability of octadecyltrichlorosilane (OTS) modified ITO substrates, and help to gain the continuous and oriented poly[2,5‐bis(4‐tetradecyloctadecyl)pyrrolo[3,4‐c]pyrrole‐1,4(2H,5H)‐dione‐alt‐5,5′‐di(thiophen‐2‐yl)‐2,2′‐(E)‐1,2‐bis(3,4‐difluorothien‐2‐yl)‐ethene] (P4FTVT‐C32) semiconductor thin films. Therefore, P4FTVT‐C32 based OTFTs with maximum electron field‐effect mobility of 1.95 cm2 V−1 s−1 are achieved by PEI treatments. These results indicate that the ITO S/D electrodes modified by nitrogenous interlayers can greatly slash costs and promote commercialization of OTFTs.

Nitrogenous Interlayers for ITO S/D Electrodes in N‐Type Organic Thin Film Transistors

Modification of Indium Tin Oxide Surface with HCl for Source/Drain Electrodes in Organic Thin Film Transistors

Complementary Inverter Based on n‐Type and p‐Type OFETs with the Same Ambipolar Organic Semiconductor and ITO S/D Electrodes

Improving the Performance of Organic Thin-Film Transistor with a Doped Interlayer

Doping Indium Oxide Films with Amino‐Polymers of Varying Nitrogen Content Markedly Affects Charge Transport and Mechanical Flexibility

A high-performance organic thin-film transistor with Parylene/PMMA bilayer insulation based on P3HT

Specific contact resistivity reduction in amorphous IGZO thin-film transistors through a TiN/IGTO heterogeneous interlayer

Improved Performance Of P-Type Pentacene Thin Film Transistor By Inserting Thin Interlayer Of N-Type Organic Semiconductor

Preparation and Application of Organic-Inorganic Nanocomposite Materials in Stretched Organic Thin Film Transistors

Electron Injection Improvement of n-Type Organic Field-Effect Transistors With Indium Contact Interlayer

Air- and Active Hydrogen-Induced Electron Trapping and Operational Instability in n-Type Polymer Field-Effect Transistors

Fused Bithiophene Imide Dimer-Based n-Type Polymers for High-Performance Organic Electrochemical Transistors

Flexible Organic Thin-Film Transistors with High Mechanical Stability on Polyimide Substrate by Chemically Plated Silver Electrodes

Tuning Interfacial Properties by Spontaneously Generated Organic Interlayers in Top‐Contact‐Structured Organic Transistors

Inkjet Printed Fine Silver Electrodes for All-Solution-Processed Low-Voltage Organic Thin Film Transistors

Significant Improvement of 2,9-Dph-dntt Organic Thin-Film Transistors Based on Organic Heterojunction Buffer Layer

Effects of Source/Drain Electrodes on the Performance of InSnO Thin-Film Transistors

Anodized ITO Thin‐Film Transistors

P‐1.1: Co‐sputtering‐deposited Hf‐doped ITO Thin Films for Thin Film Transistors Application

Direct Patterning on Top-Gate Organic Thin-Film Transistors: Improvement of On/Off Ratio, Subthreshold Swing, and Uniformity

The Strong Continuous Induction Effect Based on Isotype Heterojunction Transistors with Different Polymer Modifications