Abstract:A series of activated-carbon-supported K-Co-Mo catalysts (K-Co-Mo/AC) were prepared by using a solgel method combined with incipient wetness impregnation. The catalyst structure was characterized by X-ray diffraction (XRD), N-2 adsorption-desorption, X-ray absorption fine structure spectroscopy and X-ray photoelectron spectroscopy, and their catalytic performance toward synthesis of higher alcohols from syngas was investigated. The large surface area and pore volume of the support facilitated the distribution of metal particles and high dispersion of metals. At low Mo loading, the Mo atoms on the activated carbon surface were mainly tetrahedrally coordinated Mo6+ species. With an increase in the Mo loading, the coordination environment of the surface Mo atoms gradually transformed from tetrahedrally coordinated Mo6+ to octahedrally coordinated Mo4+, indicating that an increase in the Mo loading promoted the reduction of Mo6+ species to Mo4+ species. After reduction, it was observed that a type of a lower state Mo delta+ (1 < delta < 4) species was present on the surface, which is suggested to be responsible for alcohol synthesis. Compared to the unsupported catalyst, K-Co-Mo/AC exhibited a significantly higher activity for alcohol formation. In particular, the C2+ alcohol content increased significantly. This can be attributed to the fact that the supported catalysts have a high active surface area, and the mesoporous structure is suggested to prolong the residence time of intermediates to form alcohols in the pores to some extent, thus promoting the formation of higher alcohols. Under the conditions of a Mo/AC weight ratio of 40% and a reduction temperature of 798 K, the K-Co-Mo/AC catalyst exhibited the highest activity for alcohol formation, which may be attributed to the high content of Mo delta+ (1 < delta < 4) species on the surface.

Transition metal promoted K/Mo 2 C as efficient catalysts for CO hydrogenation to higher alcohols

Synthesis of Higher Alcohols from CO 2 Hydrogenation over Mo–Co–K Sulfide-Based Catalysts

Effect of KCoMoS2 Catalyst Structures on the Catalytic Performance of Higher Alcohols Synthesis via CO Hydrogenation

Effect of Mn Promoter on Structure and Performance of K-Co-Mo Catalyst for Synthesis of Higher Alcohols from CO Hydrogenation

Effect of cobalt promoter on Co–Mo–K/C catalysts used for mixed alcohol synthesis

Activated Carbon‐Supported Mo‐Co‐K Sulfide Catalysts for Synthesizing Higher Alcohols from CO2

A highly active K-Co-Mo/C catalyst for mixed alcohol synthesis from CO + H2.

Edge-rich molybdenum disulfide tailors carbon-chain growth for selective hydrogenation of carbon monoxide to higher alcohols

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation

Tuning the metal–support interaction in supported K-promoted NiMo catalysts for enhanced selectivity and productivity towards higher alcohols in CO hydrogenation

Ordered mesoporous NiMg bimetal oxides confined KMoS catalyst for selective CO hydrogenation into higher alcohols

Sol–gel Preparation of K–Co–Mo Catalyst and Its Application in Mixed Alcohol Synthesis from CO Hydrogenation

Effects of Cobalt Promoter and Reduction Temperature on the Surface Species and Syngas Adsorption of K–Co–Mo/C Catalyst for Mixed Alcohols Synthesis

Catalytic Properties and Structure of the K-Co-Mo Catalysts Prepared by Sol-Gel Method for Mixed Alcohol Synthesis — Effect of K Content

Activated-Carbon-Supported K-Co-Mo Catalysts For Synthesis Of Higher Alcohols From Syngas

Effects of Activation Atmospheres on Structure and Activity of Mo-based Catalyst for Synthesis of Higher Alcohols

Synthesis of Higher Alcohols from Syngas over Alkali Promoted K-Co-Mo Catalysts Supported on Multi-Walled Carbon Nanotubes

Mixed Alcohol Synthesis from Syngas on K–Co–Mo/C Catalyst Prepared by a Sol–Gel Method

Synthesis of higher alcohols by CO hydrogenation on a K-promoted Ni–Mo catalyst derived from Ni–Mo phyllosilicate

Carbon modified active pairs of Co-Co2C for CO2 hydrogenation to alcohols

Structural evolution of bimetallic Co-Cu catalysts in CO hydrogenation to higher alcohols at high pressure