Abstract:A series of activated-carbon-supported K-Co-Mo catalysts (K-Co-Mo/AC) were prepared by using a solgel method combined with incipient wetness impregnation. The catalyst structure was characterized by X-ray diffraction (XRD), N-2 adsorption-desorption, X-ray absorption fine structure spectroscopy and X-ray photoelectron spectroscopy, and their catalytic performance toward synthesis of higher alcohols from syngas was investigated. The large surface area and pore volume of the support facilitated the distribution of metal particles and high dispersion of metals. At low Mo loading, the Mo atoms on the activated carbon surface were mainly tetrahedrally coordinated Mo6+ species. With an increase in the Mo loading, the coordination environment of the surface Mo atoms gradually transformed from tetrahedrally coordinated Mo6+ to octahedrally coordinated Mo4+, indicating that an increase in the Mo loading promoted the reduction of Mo6+ species to Mo4+ species. After reduction, it was observed that a type of a lower state Mo delta+ (1 < delta < 4) species was present on the surface, which is suggested to be responsible for alcohol synthesis. Compared to the unsupported catalyst, K-Co-Mo/AC exhibited a significantly higher activity for alcohol formation. In particular, the C2+ alcohol content increased significantly. This can be attributed to the fact that the supported catalysts have a high active surface area, and the mesoporous structure is suggested to prolong the residence time of intermediates to form alcohols in the pores to some extent, thus promoting the formation of higher alcohols. Under the conditions of a Mo/AC weight ratio of 40% and a reduction temperature of 798 K, the K-Co-Mo/AC catalyst exhibited the highest activity for alcohol formation, which may be attributed to the high content of Mo delta+ (1 < delta < 4) species on the surface.

Synthesis of higher alcohols by CO hydrogenation on a K-promoted Ni–Mo catalyst derived from Ni–Mo phyllosilicate

Synthesis of Higher Alcohols from CO 2 Hydrogenation over Mo–Co–K Sulfide-Based Catalysts

Ordered mesoporous NiMg bimetal oxides confined KMoS catalyst for selective CO hydrogenation into higher alcohols

Effect of cobalt promoter on Co–Mo–K/C catalysts used for mixed alcohol synthesis

Activated Carbon‐Supported Mo‐Co‐K Sulfide Catalysts for Synthesizing Higher Alcohols from CO2

Synthesis of Higher Alcohols from Syngas over Alkali Promoted K-Co-Mo Catalysts Supported on Multi-Walled Carbon Nanotubes

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation

Sol–gel Preparation of K–Co–Mo Catalyst and Its Application in Mixed Alcohol Synthesis from CO Hydrogenation

Effect of KCoMoS2 Catalyst Structures on the Catalytic Performance of Higher Alcohols Synthesis via CO Hydrogenation

CO Hydrogenation to Higher Alcohols over Ni- and Mo-modified Cu/CeO 2 Catalyst

Mixed Alcohol Synthesis from Syngas on K–Co–Mo/C Catalyst Prepared by a Sol–Gel Method

Nanosheet-structured K–Co–MoS2 Catalyst for the Higher Alcohol Synthesis from Syngas: Synthesis and Activation

Co–Co2C catalysts supported on carbon-coated ordered mesoporous silica with promoted CO insertion and C–C coupling for higher alcohol synthesis from syngas

Effect of Mn Promoter on Structure and Performance of K-Co-Mo Catalyst for Synthesis of Higher Alcohols from CO Hydrogenation

Targeted Design And Synthesis Of A Highly Selective Mo-Based Catalyst For The Synthesis Of Higher Alcohols

Activated-Carbon-Supported K-Co-Mo Catalysts For Synthesis Of Higher Alcohols From Syngas

Tuning the metal–support interaction in supported K-promoted NiMo catalysts for enhanced selectivity and productivity towards higher alcohols in CO hydrogenation

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Effects of Activation Atmospheres on Structure and Activity of Mo-based Catalyst for Synthesis of Higher Alcohols

Bimetallic Ni–Co catalysts supported on Mn–Al oxide for selective catalytic CO hydrogenation to higher alcohols

Graphene oxide-ordered mesoporous silica composite supported Co-based catalysts for CO hydrogenation to higher alcohols