Abstract:Bimetallic CoCu model catalysts were investigated for the synthesis of higher alcohols using catalytic CO hydrogenation according to the Fischer–Tropsch technology. Emphasis was placed on revealing the influence of the activation conditions. Accordingly, catalyst precursors were activated in argon, hydrogen, syngas (CO/H2), and CO under atmospheric conditions and at elevated temperatures (370 °C). All catalyst precursors were prepared via oxalate coprecipitation in the absence of a classic support. Alcohol selectivities between 30 and ∼40% (up to ∼50% for the sum of alcohols and alkenes) were obtained with an Anderson–Schulz–Flory (ASF) chain lengthening probability maximizing the slate up to C6. Detailed catalysis and characterization studies were performed using a Co2Cu1 catalyst composition. The catalytic performances of the H2- and syngas-activated Co2Cu1 catalyst were similar. While the CO-activated catalyst shows significantly higher catalytic activity and ASF chain lengthening probability, the alcohol selectivities are lower than those of H2- or syngas-activated ones. All catalysts required time on stream for several hours to achieve steady-state catalytic performance. Co2Cu1 catalysts were characterized by temperature-programmed decomposition (TPDec), in situ N2 physisorption (Brunauer–Emmett–Teller), transmission electron microscopy (TEM), and in situ X-ray photoelectron spectroscopy (XPS). The data indicate major restructuring occurs during activation. An “onion-like” graphitic carbon shell was observed via TEM for the CO-activated Co2Cu1 catalyst, which probably originated mainly from the Boudouard reaction (2CO + [ ]ad → Cad + CO2). This interpretation is in accordance with the TPDec profiles and XPS results. The latter also indicates that syngas and CO activation lead to higher than nominal Co/Cu surface ratios. The surface segregation of Co in the presence of CO atmospheres is interpreted on the basis of Co@Cu core–shell structured particles.

Effects of Activation Atmospheres on Structure and Activity of Mo-based Catalyst for Synthesis of Higher Alcohols

Activated-Carbon-Supported K-Co-Mo Catalysts For Synthesis Of Higher Alcohols From Syngas

Effect of Mn Promoter on Structure and Performance of K-Co-Mo Catalyst for Synthesis of Higher Alcohols from CO Hydrogenation

Enhanced CH4 Production from CO2 Hydrogenation on Γ-Alooh-supported Cobalt Catalyst with Abundant Surface Coordination Unsaturated Oxygen Atoms

Effects of Cobalt Promoter and Reduction Temperature on the Surface Species and Syngas Adsorption of K–Co–Mo/C Catalyst for Mixed Alcohols Synthesis

Effect of cobalt promoter on Co–Mo–K/C catalysts used for mixed alcohol synthesis

Effect of KCoMoS2 Catalyst Structures on the Catalytic Performance of Higher Alcohols Synthesis via CO Hydrogenation

Nanosheet-structured K–Co–MoS2 Catalyst for the Higher Alcohol Synthesis from Syngas: Synthesis and Activation

Clay-Supported Molybdenum-Based Catalysts for Higher Alcohol Synthesis from Syngas

Activated Carbon‐Supported Mo‐Co‐K Sulfide Catalysts for Synthesizing Higher Alcohols from CO2

Synthesis of Higher Alcohols from Syngas over Alkali Promoted K-Co-Mo Catalysts Supported on Multi-Walled Carbon Nanotubes

Mixed Alcohol Synthesis from Syngas on K–Co–Mo/C Catalyst Prepared by a Sol–Gel Method

Sol–gel Preparation of K–Co–Mo Catalyst and Its Application in Mixed Alcohol Synthesis from CO Hydrogenation

Synthesis of Higher Alcohols from CO 2 Hydrogenation over Mo–Co–K Sulfide-Based Catalysts

Targeted Design And Synthesis Of A Highly Selective Mo-Based Catalyst For The Synthesis Of Higher Alcohols

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation

Influence of Co Modified Mn/Cu/MgO Catalyst on the Synthesis of Mixed Alcohols from Syngas

Synthesis of higher alcohols by CO hydrogenation on a K-promoted Ni–Mo catalyst derived from Ni–Mo phyllosilicate

Catalytic Properties and Structure of the K-Co-Mo Catalysts Prepared by Sol-Gel Method for Mixed Alcohol Synthesis — Effect of K Content