Abstract:Currently, the Cu-based catalyst has become a promising candidate for ethanol and higher alcohols synthesis (HAs) from synthesis gas (H2 + CO), but all these catalysts contain F–T elements (e.g., Co and Fe) and alkalis because carbon chain growth reaction occurs on these metal components. Herein, two series of ternary CuZnAlOOH catalysts with various Cu and Al proportions were synthesized using a complete liquid-phase method and studied in the conversion of syngas in a slurry bed reactor. Significantly higher selectivity of ethanol (40 wt %) and HA (65 wt %) with approximately 20% CO conversion was achieved when the n(Cu)/n(Al) = 2/0.8, which was ascribed the highest copper surface area (SCu) and the surface Cu content. It was found that the Cu component had a significant effect on CO conversion, while the Al component had more influence on the selectivity of HA. Besides, the coke deposition was discovered to be the main reason for catalyst deactivation. The generation of hydrocarbons and alcohols followed A–S–F distributions, which was consistent with a representative mechanism of HA generation by CO insertion into the CHx intermediate. A synergetic mechanism between Cu0–Cu+ and AlOOH active sites was proposed based on the characterization analysis and activity results, in which Cu0–Cu+ synergy acted as sites for H2 dissociative adsorption and associative adsorption of CO, while the AlOOH facilitated the dissociation of the C–O bond. Bifunctionality of the Cu and AlOOH active sites and their cooperation created their synergy in CO hydrogenation to ethanol and HA. This work provided us a new concept to understand and develop carbon chain growth mechanism, and it also could provide reference for other related carbon chain growth reactions.

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Effects of alkali promoters on tri-metallic Co-Ni-Cu-based perovskite catalyst for higher alcohol synthesis from syngas

Effect of K and Ni Promoters on Mo2C/Al2O3 Catalyst for Higher Alcohols Synthesis from Syngas

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

CuZnAl@S-1 Catalyst for the Synthesis of Higher Alcohols by CO Hydrogenation

Higher Alcohols Synthesis from Syngas over Cocu/Sio2 Catalysts: Dynamic Structure and the Role of Cu

Electron promoted ZnO for catalytic synthesis of higher alcohols from syngas

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

Selective Synthesis of Methanol and Higher Alcohols over Cs/Cu/ZnO/Al2O3 Catalysts

Perovskite-derived trimetallic Co-Ni-Cu catalyst for higher alcohol synthesis from syngas

The Support Effects on the Direct Conversion of Syngas to Higher Alcohol Synthesis over Copper-Based Catalysts

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

Investigation of Al precursor for ethanol synthesis from syngas on Cu-based multifunctional catalyst

Synergistic Effect of Nitrogen-Doped Carbon-Nanotube-supported Cu–Fe Catalyst for the Synthesis of Higher Alcohols from Syngas

Copper–cobalt catalysts supported on mechanically mixed HZSM-5 and γ-Al2O3 for higher alcohols synthesis via carbon monoxide hydrogenation

Syngas conversion to higher alcohols via wood-framed Cu/Co-carbon catalyst

Influence of Co Modified Mn/Cu/MgO Catalyst on the Synthesis of Mixed Alcohols from Syngas

Conversion of Syngas to C1-C6 Alcohol Mixtures on Promoted CuLa2Zr2O7 Catalysts