Abstract:Lanthanum hexaboride (LaB6) as an excellent thermionic electron emitter was characterized by high brightness, thermal stability, low volatility and high mechanical strength [1]. The advantages are originated from its low work function (2.4 eV~2.6 eV), high melting point (2715 °C) and covalent bond of B-B atom in crystal structure. Recently, many researchers focused their attention on the excellent field emission properties of LaB6 one-dimensional nanoelectronics as well as nanomachine applications . Late et al.[3] have reported the LaB6 tips and foils grown on tungsten and rhenium substrate by Pulsed laser deposition (PLD) at temperature 700°C with average grain size ~ 125nm. However, there are some disadvantages of above-mentioned methods. The BCI3 as the boron source is easy to absorb water and convert into boric acid, which resist the reaction. The stoichiometry of the products was hard to control by gaseous starting materials. For thin films, there have some intrinsic disadvantages, including poor adhesion to the substrate and oxide contained in the emitter. Compared to the nanowires and nanofilms, the bulk materials can provide large size, low cost, simple preparation. Therefore, there are great research prospects for polycrystalline LaB6 Field emission properties. The polycrystalline LaB6 bulk material was prepared by SPS method. The LaB6 field emitting single tip has been achieved using the electrochemical etching method. Figure 1 shows the relative density of 95.5% and 99.2% corrosion morphology. It is seen from the figure 1 that the low-density samples have a large number of corrosion holes and surface defects, showing anisotropic corrosion characteristic. This is due to the corrosion process, the etching solutions immerse to the holes to lateral erosion, which directly led to the tip radius of about 10μm. The relative density of 99.2% of tip shows that cor- osion of the sample is uniform and surface is smooth, the tip radius is about 2μm. Fig. 2 shows the tip field emission current and applied voltage curves. It is seen that when the voltage is 1200 V (electric field strength of 12 V / μm) there occurs emission current and the current increased with the voltage When the voltage is increased to 1700 V (electric field strength of 17 V / μm), the emission current was 16 μA and don't reach saturation. Fig.3 shows the results of surface electric field distribution.

Characterization of a LaB6 tip as a thermionically enhanced photoemitter

Wehnelt Photoemission in an Ultrafast Electron Microscope: Stability and Usability

Field Emission Characteristics of Polycrystalline LaB6 Single Tip and Surface Electric Field Distribution

An ultrabright and monochromatic electron point source made of a LaB 6 nanowire

Gravitational instability of static spherically symmetric Einstein-Gauss-Bonnet black holes in five and six dimensions

Field Emission Characteristics of LaB6 Single Tip Emitter

Field Emission Investigations of Single Crystal LaB6 FEA Fabricated by Femtosecond Laser Direct Writing

Electrical and thermal characteristics of LaB6 thermionic hollow cathodes operating in He, D2, Ar, and Xe at 4–200 Pa and 0.25–5 A cm−2

Fabrication of Lanthanum Hexaboride Single Nanowire Field Emitter and Their Field Emission Properties

New Applications for Ultra-High Brightness LaB6 Nanowire Cathode

Laser-induced Field Emission from Tungsten Tip: Optical Control of Emission Sites and Emission Process

Laser-driven cold-field emission source for ultrafast transmission electron microscopy

Tunable ultrafast thermionic emission from femtosecond-laser hot spot on a metal surface: role of laser polarization and angle of incidence

Electron Kinetics Induced by Ultrafast Photoexcitation of Warm Dense Matter in a 30-Nm-thick Foil.

LaB6 Nanowires and Their Field Emission Properties

Improved field electron emission behavior of ultrathin lanthanum hexaboride-coated copper oxide nanowires

Electron emission from the oxide-coated cathode under the laser illumination

Pulse Thermionic Emission Performance of Multi-Crystal LaB6 Cathode

Ultrafast Dynamics of Thermionic Emission on Au Film under Femtosecond Laser Excitation

Study Of X-Ray Emission Enhancement Via A High-Contrast Femtosecond Laser Interacting With A Solid Foil

Tracing attosecond electron emission from a nanometric metal tip