Abstract:The bio-corrosion behavior and bio-compatibility of TiNbZrTa and TiNbZrTaMo high entropy alloys (HEAs) are crucial for their efficient maintenance during biological implantation. In this work, TiNbZrTa and TiNbZrTaMo HEAs were successfully prepared via vacuum melting, with a beta-type titanium alloy Ti35Nb7Zr5Ta, exhibiting good biocompatibility used as a comparison. Due to the high entropy effect of equal atomic ratios, both TiNbZrTa and TiNbZrTaMo HEAs exhibit body-centered cubic (BCC) structure and lattice distortion compared to the beta titanium alloy Ti35Nb7Zr5Ta. Mo elements contribute to the formation of a new BCC phase, resulting in a white matrix rich in Ta and Mo, and a dark second phase rich in Ti, Zr, and Nb. Electrochemical test results at 37 degrees C shown that TiNbZrTa has a wider and more stable passivation area than TiNbZrTaMo. The XPS results shown that formation of the passive film is related to the main elements added. Ti, Nb, Ta and Mo formed oxides via the solid-liquid interface and migrate inward, while Zr is formed at the passivation film/metal substrate interface and migrates outward, finally forming the layered structure of the passivation film. Additionally, the cytotoxicity test of mouse fiber cells was carried out to evaluate the biocompatibility of the HEAs. The results shown that the cell proliferation rate of TiNbZrTa and TiNbZrTaMo HEAs reached 0 and 1, respectively, with TiNbZrTa exhibiting better biocompatibility, as adding Mo reduced the cell proliferation rate. These findings may provide a method for predicting the bio-corrosion behavior and bio-compatibility of HEAs used for biological implantation.

Electrochemical corrosion and high temperature hot corrosion behavior of NbTaTiV and CrNbTaTiV high entropy alloy

Effect of Nb and Cu on α/β Phase Transition Temperature and Corrosion Behavior of New Type Zirconium Alloys

Synthesis and corrosion behavior of Mo15Nb20Ta10Ti35V20 refractory high entropy alloy

Bio-Corrosion Behaviors and Bio-Compatibilities of Tinbzrta and Tinbzrtamo High Entropy Alloys

Hot Corrosion and Electrochemical Behavior of NiCrAlY, NiCoCrAlY and NiCoCrAlYTa Coatings in Molten NaCl-Na2SO4 at 800 °C

Electrochemical study on the hot corrosion behavior of Ni16Cr13Co4Mo alloy in molten NaCl-KCl and NaCl-KCl-Na2SO4

Corrosion Resistance of Nb and NbTi Alloy Predicted by Hydrogen Evolution Reaction Models Modified with Langmuir Isotherm Adsorption Theory

The high temperature wetting and corrosion mechanism analysis of Nb by TiAl alloy melt

Microstructure and Corrosion Behavior of the Ti-V-Cr-Nb High-Entropy Alloys in 3.5 wt.% NaCl Solution

Thermal stability and corrosion behavior of a novel Zr22.5Ti22.5Hf22.5Ni22.5Ta10 high-entropy amorphous alloy

Electrochemical and XPS studies of a Nb-containing Ti-based glass-forming alloy system in H 2 SO 4 solution

An investigation on hot corrosion behavior of Al 0.4 MnCrCoFeNi high entropy alloy in different molten salts at 750 °C

Studies on Corrosion Behavior of a Single-Crystal Superalloy and Its Sputtered Nanocrystalline Coatings with Solid NaCl Deposit in O2 + 38 Vol.% H2O Environment at 700 °C

High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy

Corrosion Behaviors of Mo0.5NbTiVCr0.25 and Mo0.5NbTiV0.5Zr0.25 Multi Principal Element Alloys in High Temperature Borated and Lithiated Water

Thermal and corrosion properties of V-Nb-Mo-Ta-W and V-Nb-Mo-Ta-W-Cr-B high entropy alloy coatings

NaCl-induced hot corrosion of a titanium aluminide alloy

Corrosion and passive behaviors of the Co-Cr-Fe-Ni-Nb eutectic high-entropy alloys in different electrolyte solutions

Influence of Nb on the Hot Corrosion Behaviors of a Fe–Cr–Ni Heat-Resistant Steel Weld Metal in the Na2SO4–NaCl Molten Salt at 700 °C

Addition of niobium in Fe-13Cr-4.5Al-2Mo alloy used as ATF cladding: Effect on high temperature water corrosion and in-situ electrochemistry

Effect of Cr Content on Microstructure and Properties of Mo0.5VNbTiCrx High-Entropy Alloys