Hot salt corrosion behavior of the Ti-44Al-4Nb-1.5Mo-(B,Y) alloy in the temperature range of 750–950 °C

By Yefei Zhang,Haitao Jiang,Siyuan Zhang,Zhenyu Yang,Tengkun Zhang,Shiwei Tian
DOI: https://doi.org/10.1016/j.jmrt.2023.08.220
IF: 6.267
2023-09-03
Journal of Materials Research and Technology
Abstract:Hot salt corrosion behavior of TNM alloy (Ti-44Al-4Nb-1.5Mo-(B, Y) (at.%)) was investigated in cyclic conditions at 750 °C, 850 °C and 950 °C for 100 h in the 75 wt% Na 2 SO 4 + 25 wt% NaCl salt mixture. The hot salt corrosion resistance of γ、α 2 and β phase in the alloy was studied by short-term quasi-in-situ hot corrosion experiments. Results show that the hot salt corrosion resistance of the three phases decreases in the following order: γ、α 2 、β. The weight changes of TNM alloy after hot salt corrosion at 750 °C, 850 °C and 950 °C for 100 h are 13.8 mg/cm 2 , -19.6 mg/cm 2 and -26.7 mg/cm 2 . Under the condition of hot salt corrosion at 750 °C, the corrosion scales are mainly composed of a mixed corrosion scale of TiO 2 and Al 2 O 3 , Al 2 O 3 scale, and Al depletion zone, similar to the morphology of a high-temperature oxidation scale. The corrosion scales are seriously peeled off and destructive transverse cracks are generated inside the corrosion scales under the conditions of hot salt corrosion at 850 °C and 950 °C. The acid-base corrosion dissolution of oxides in the corrosive medium and the formation of volatile chlorides are the main causes of cracks in the TiO 2 and Al 2 O 3 scales. In addition, the Nb element in the TNM alloy is mainly enriched beneath the corrosion scales to form a NaNbO 3 layer, which can inhibit the decomposition and penetration of the corrosive medium. Mo element reacts with the S element to form MoS 2 , which anchors the S element to a certain extent.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?