Abstract:A pristine colusite Cu26V2Sn6S32 was successfully synthesised on a 100 g scale via a mechanochemical reaction in an industrial eccentric vibratory ball mill followed by spark plasma sintering (SPS) at 873 K. The milling of elemental precursors from 1 up to 12 hours was performed and the prepared samples were investigated in detail by X-ray powder diffraction, Mössbauer spectroscopy, scanning electron microscopy, and thermoelectric property measurements. The results point to the formation of a high purity and high crystallinity non-exsoluted colusite phase after the SPS process (P4[combining macron]3n, a = 10.7614(1) Å) in the case of a 12 h milled sample. In comparison, samples milled for 1-6 h displayed small quantities of binary Cu-S phases and vanadium core-shell inclusions, leading to a V-poor/Sn-rich colusite with a higher degree of structural disorder. These samples exhibit lower electrical conductivity and Seebeck coefficient while an increase in the total thermal conductivity is observed. This phenomenon is explained by a higher reactivity and grain size reduction upon prolonged milling and by a weak evolution of the chemical composition from a partly disordered V-poor/Sn-rich colusite phase to a well-ordered stoichiometric Cu26V2Sn6S32 colusite, which leads to a decrease in carrier concentration. For all samples, the calculated PF values, around 0.7-0.8 mW m-1 K-2 at 700 K, are comparable to the values previously achieved for mechanochemically synthesised Cu26V2Sn6S32 in laboratory mills. This approach thus serves as an example of scaling-up possibility for sulphur-based TE materials and supports their future large-scale deployment.

Ultrafast synthesis of Pb-doped BiCuSeO oxyselenides by high-energy ball milling

Direct synthesis of p-type bulk BiCuSeO oxyselenides by reactive spark plasma sintering and related thermoelectric properties

Enhanced Thermoelectric Properties in Pb-doped BiCuSeO Oxyselenides Prepared by Ultrafast Synthesis

Microwave synthesis combined with SPS sintering to fabricate Pb doped p-type BiCuSeO oxyselenides thermoelectric bulks in a few minutes

Rapid and direct synthesis of complex perovskite oxides through a highly energetic planetary milling

Microwave Synthesis and Enhanced Thermoelectric Performance of p-Type Bi 0.90 Pb 0.10 Cu 1- x Fe x SeO Oxyselenides

A facile top-down synthesis of phase pure CuBi2O4 photocathode materials by low-energy sequential ball milling

Ultra-Fast Synthesis and High Thermoelectric Properties of Heavy Sodium Doped Bicuseo

Mechanical Alloying and Spark Plasma Sintering of Bicuseo Oxyselenide: Synthesis Process and Thermoelectric Properties

Thermoelectric properties of Bi 1− x Pb x Cu 1− x SeO oxyselenides

One-step synthesis of all-inorganic high-entropy dual-phase Cs‘B’Br3/Cs‘B’2Br5 perovskite nanocrystals by high-energy ball milling

Synergistically optimized electron and phonon transport of p-type BiCuSeO oxyselenides via Pb dopant and Te composite

Combinatorial Synthesis of Oxysulfides in the Lanthanum-Bismuth-Copper System

Synthesis of Nd0.7Sr0.3MnO3 Ceramics by High-Energy Ball Milling

Ultrafast high-temperature sintering of bulk oxides

Time-dependent investigation of a mechanochemical synthesis of bismuth telluride-based materials and their structural and thermoelectric properties

Ultrafast high-temperature sintering of lanthanum-chromite-based ceramics

MECHANOCHEMICAL SYNTHESIS OF CEO2 NANOPOWDER USING PLANETARY BALL MILLING

Preliminary Study of 3d Ball-Milled Powder Processing and Sps-Accelerated Densification of Znse Ceramics

Promoted crystallisation and cationic ordering in thermoelectric Cu26V2Sn6S32 colusite by eccentric vibratory ball milling

Optimization of high-energy ball milling process for uniform p-type Bi-Sb-Te thermoelectric material powder