Time-dependent investigation of a mechanochemical synthesis of bismuth telluride-based materials and their structural and thermoelectric properties

Dennis Groeneveld,Jan D. Koenig,Michael Poschmann,Hendrik Groß,Wolfgang Bensch,Lorenz Kienle,Jürgen Wöllenstein

DOI: https://doi.org/10.1098/rsos.210714

IF: 3.5

2022-03-01

Royal Society Open Science

Abstract:Here, we report on the time dependence of a synthesis procedure for generation of both n- and p-type bismuth telluride-based materials. To initiate the reaction, the starting materials were first mechanical pre-reacted. The Rietveld refinements of X-ray diffraction (XRD) data collected after different milling times demonstrate that Bi 2 Te 3 was formed after only 10 min, and longer milling times do not alter the composition. To complete the phase formation, the powders were treated by field-assisted sintering and heat treatment afterwards. The effect of this fast procedure on the structural and thermoelectric properties was investigated. Samples were obtained with relative densities above 99%. A clear preferred orientation of the crystallites in the samples is evidenced by Rietveld refinements of XRD data. The thermoelectric characteristics demonstrate a good performance despite the short milling time. Further, it was demonstrated for this fast synthesis that the physical transport properties can be varied with well-known n- and p-type dopants like CHI 3 or Pb. For these non-optimized materials, a ZT value of 0.7 (n-type) and 0.9 (p-type) between 400 and 450 K was achieved. The long-term stability is demonstrated by repeated measurements up to 523 K showing no significant alteration of the thermoelectric performance.

multidisciplinary sciences