Abstract:Bi2Te3-based materials are dominating thermoelectrics for almost all of the room-temperature applications. To meet the future demands, both their thermoelectric (TE) and mechanical properties need to be further improved, which are the requisite for efficient TE modules applied in areas such as reliable micro-cooling. The conventional zone melting (ZM) and powder metallurgy (PM) methods fall short in preparing Bi2Te3-based alloys, which have both a highly textured structure for high TE properties and a fine-grained microstructure for high mechanical properties. Herein, a mechanical exfoliation combined with spark plasma sintering (ME-SPS) method is developed to prepare Bi0.5Sb1.5Te3 with highly improved mechanical properties (correlated mainly to the dislocation networks), as well as significantly improved thermoelectric properties (correlated mainly to the texture structure). In the method, both the dislocation density and the orientation factor (F) can be tuned by the sintering pressure. At a sintering pressure of 20 MPa, an exceptional F of up to 0.8 is retained, leading to an excellent power factor of 4.8 mW m-1 K-2 that is much higher than that of the PM polycrystalline. Meanwhile, the method can readily induce high-density dislocations (up to ∼1010 cm-2), improving the mechanical properties and reducing the lattice thermal conductivity as compared to the ZM ingot. In the exfoliated and then sintered (20 MPa) sample, the figure-of-merit ZT = 1.2 (at 350 K), which has increased by about ∼20%, and the compressive strength has also increased by ∼20%, compared to those of the ZM ingot, respectively. These results demonstrate that the ME-SPS method is highly effective in preparing high-performance Bi2Te3-based alloys, which are critical for TE modules in commercial applications at near-room temperature.

Optimization of high-energy ball milling process for uniform p-type Bi-Sb-Te thermoelectric material powder

Enhanced thermoelectric performance of n -type PbTe bulk materials fabricated by semisolid powder processing

Microstructure and thermoelectric properties of porous Bi 2 Te 2.85 Se 0.15 bulk materials fabricated by semisolid powder processing

High Thermoelectric Performance of p-Type Bi0.4Sb1.6Te3+ x Synthesized by Plasma-Assisted Ball Milling

Enhancing Thermoelectric Properties of Polycrystalline Bi 2 S 3 by Optimizing a Ball-Milling Process

Mechanically Enhanced P- and N-Type Bi2Te3-based Thermoelectric Materials Reprocessed from Commercial Ingots by Ball Milling and Spark Plasma Sintering

Synthesis and thermoelectric properties of bismuth antimony telluride thermoelectric materials fabricated at various ball-milling speeds with yttria-stabilized zirconia ceramic vessel and balls

Microstructure and thermoelectric performance evaluation of p-type (Bi, Sb)2Te3 materials synthesized using mechanical alloying and spark plasma sintering process

Thermoelectric Properties of Off-Stoichiometric Bi2Te2Se Compounds

Effect of ball milling time on thermoelectric properties of bismuth telluride nanomaterials

Preparation and characterization of high T c (1-x) BiScO 3-xPbTiO3 ceramics from high energy ball milling process

Enhancing the Thermoelectric and Mechanical Properties of Bi 0.5 Sb 1.5 Te 3 Modulated by the Texture and Dense Dislocation Networks

Microstructure Evolution in Plastic Deformed Bismuth Telluride for the Enhancement of Thermoelectric Properties

Enhancing the thermoelectric properties of bismuth antimony tellurides containing excess Te with respect to sintering temperature

Preparation and study of nanodispersed powders of thermoelectric materials

Cold-Sintered Bi 2 Te 3 -Based Materials for Engineering Nanograined Thermoelectrics

Modulation of Vacancy Defects and Texture for High Performance n‐Type Bi2Te3 via High Energy Refinement

Analysis of Thermoelectric Properties of Hot-deformed Bismuth Telluride Sintered Materials

Continuous and Intermittent Planetary Ball Milling Effects on the Alloying of a Bismuth Antimony Telluride Powder Mixture

Mn15Bi34Te51 and La15Bi34Te51 thermoelectric materials by mechanical alloying

Synergistically Optimized Thermoelectric and Mechanical Properties in p ‐Type BiSbTe by a Microdroplet Deposition Technique