Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Precipitated Silica from Sodium Silicate by CO2 on Fixed Bed Column

Performance of Nano-Caco3 Coated with SiO2 on CO2 Adsorption at High Temperature

Study on preparation and surface modification of precipitated silica obtained from fly ash

Modified mesoporous silica derived from bamboo leaf using cetyltrimethylammonium bromide and 3-aminopropyl triethoxysilane as CO2 adsorbent in biogas purification

Preparation of silica xerogel with high silanol content from sodium silicate and its application as CO2 adsorbent

Preparation of highly dispersed nanosilica from rice husk by aprecipitation method combined with high pressure homogenization

Preparation of Precipitated Nano-silica from Acid Leaching Residue of Coal Ash by Carbonation Method

Preparation of Highly Dispersed Precipitated Nanosilica in a Membrane Dispersion Microreactor

Synthesis of synthetic amorphous silica powder from palm oil mill fly ash extract by carbon dioxide impregnation

Synthesis of Silica Xerogel from Geothermal Sludge by Ultrasonic Assisted Alkali Extraction-Acid Precipitation

Extraction of silica from sugarcane bagasse ash and its utilization in zeolite 4A synthesis for CO2 adsorption

Preparation and Co2 Sorption/Desorption of N-(3-Aminopropyl) Aminoethyl Tributylphosphonium Amino Acid Salt Ionic Liquids Supported into Porous Silica Particles

Sustainable route for silica preparation from silica fume

MECHANOCHEMICAL METHOD OF PROCESSING SILICA-CONTAINING PLANT MATTER

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

Sillica Gel-Amine from Geothermal Sludge

The surface structure of nanosilica produced from sodium silicate by the carbonation process

Dissolution of quartz sand in sodium hydroxide solution for producing amorphous precipitated silica

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Preparation of Silica Material with High Pore Volume by Precipitation in Membrane Dispersion Reactor

Solid‐phase synthesis of silicalite‐1 molecular sieve based on fly ash and its CO2 adsorption performance