Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Preparation of silica xerogel with high silanol content from sodium silicate and its application as CO2 adsorbent

Preparation and Co2 Sorption/Desorption of N-(3-Aminopropyl) Aminoethyl Tributylphosphonium Amino Acid Salt Ionic Liquids Supported into Porous Silica Particles

Synthesis and CO2 Adsorption Performance of Amine loaded Silica Aerogel

Preparation of Hydrophobic Hierarchical Pore Carbon–silica Composite and Its Adsorption Performance Toward Volatile Organic Compounds

Facile Co-Precursor Sol-Gel Synthesis of a Novel Amine-Modified Silica Aerogel for High Efficiency Carbon Dioxide Capture.

Direct Synthesis of Amine-functionalized Mesoporous Silica for CO2 Adsorption

Amine-functionalized Monodispersed Porous Silica Microspheres with Enhanced CO2 Adsorption Performance and Good Cyclic Stability.

Preparation and Characterization of a Novel Silica Aerogel As Adsorbent for Toxic Organic Compounds

Extraordinary Adsorption Properties of Nano Porous Hydrophobic Silica Aerogels

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance

Synthesis of Large Mesoporous Silica for Efficient CO2 Adsorption Using Coal Gasification Fine Slag

An Efficient Amine-Modified Silica Aerogel Sorbent for CO2 Capture Enhancement: Facile Synthesis, Adsorption Mechanism and Kinetics

Synthesis and CO2 adsorption property of amino-functionalized silica nanospheres with centrosymmetric radial mesopores

A Pressurized Carbonation Sol–gel Process for Preparing Large Pore Volume Silica and Its Performance As a Flatting Agent and an Adsorbent

Synthesis of hydrophilic and hydrophobic xerogels with superior properties using sodium silicate

Preparation of Nano-Porous Carbon-Silica Composites and Its Adsorption Capacity to Volatile Organic Compounds

Investigation of adsorption/desorption performance by aminopropyltriethoxysilane grafted onto different mesoporous silica for post-combustion CO2 capture

Surface Modification and Adsorption Properties of SiO2 Nanoporous Aerogels

The effect of surfactants on carbon xerogel structure and CO 2 capture

Enhanced CO2 Adsorption Property of Amine In-Situ Hybrid SiO2 Aerogels by the Incorporation of Micropores