Abstract:In this work, the tungsten-copper composites were fabricated by binder jet 3D printing technology. The effects of different printing layer thicknesses (50 mu m to 100 mu m) on the green density and green strength were investigated. Then, under the optimal layer thickness, the effects of different sintering temperatures (1300 degrees C to 1600 degrees C) on the microstructure and densification of tungsten-40 wt.-% copper composites were studied. The experimental results showed that when the printing layer thickness was set as a lower value (50 mu m), the tungsten-40 wt.-% copper green part had the best strength and its density reached a maximum value of 60.73 %. After sintering for green parts printed with 50 mu m layer thickness, the relative density, thermal conductivity and electrical conductivity of sintered parts first increased and then decreased with increasing sintering temperature. In our experiments, the tungsten-40 wt.-% copper sample fabricated by binder jet 3D printing with a printing layer thickness of 50 mu m under a sintering temperature of 1500 degrees C displayed the best properties, in which the relative density, thermal conductivity and electrical conductivity were 97.04 %, 228 W & sdot;m-1 & sdot;K-1 and 46.5 % IACS, respectively. In this work, tungsten-copper composites were prepared by binder jet 3D printing technology for the first time. By studying the effects of printing layer thickness and sintering temperature on density and properties, a tungsten-40 wt.-% copper composite with a relative density of up to 97.04 % and a thermal conductivity of 228 W & sdot;m-1 & sdot;K-1 was successfully prepared. image

Shape retention of W-30Cu composites prepared by 20 wt% Cu melt infiltration into W-10Cu green parts made via BJ3DP

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Shape Retention of Cemented Carbide Prepared by Co Melt Infiltration into Un-Sintered WC Green Parts Made Via BJ3DP

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Sintering Behavior of W–30Cu Composite Powder Prepared by Electroless Plating

Research on the densification of W-30 wt%Cu composite powder by hot extrusion with steel cup

W–Cu Composite with High W Content Prepared by Grading Rounded W Powder with Narrow Particle Size Distribution

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Effect of Silver Element on Microstructure and Properties of W-30Cu/TiC Composites

Influence of TiC Content on Microstructure and Properties of W-30Cu/TIC Composites

Formation Mechanism of W-coated Cu Composite Powders and the Metal Injection Molding Using Polyoxymethylene-Based Binders

Microstructure and Properties of Tungsten-40 Wt.-% Copper Composites Fabricated by Binder Jet 3D Printing

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Research on the densification of W–40 wt.%Cu by liquid sintering and hot-hydrostatic extrusion

Fabrication and Microstructure of C/Cu Composites

Effects of Bonding Treatment and Ball Milling on W-20 wt.% Cu Composite Powder for Injection Molding

Fabrication of 60 wt%W-40 wt%Cu composite with crystal orientation by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Microstructural studies of W–10wt.% Cu composites prepared by using ultrafine composite powder

Effect of sintering temperature on fine-grained Cu W composites with high copper

Preparation and properties of W-30 wt% Cu alloy with the additions of Ni and Fe elements

Study of a New Method to Fabricate W–Cu Composites