Abstract:A NASICON-type electrolyte was considered to be one of the most promising electrolytes for solid-state Na metal batteries. However, its lower ion conductivity compared to a liquid electrolyte and the formation of Na dendrites hinder its practical application. Herein, NASICON-type (Na3Zr2Si2PO12) solid-state electrolytes with developed ionic conductivity and declined electronic conductivity were synthesized through the rare earth oxide-assisted sintering method, such as Sm2O3 and Ho2O3. With the presence of Sm2O3 and Ho2O3 during sintering, the formed phosphate grain boundary phase adjusts the Si/P ratio in the NASICON structure with higher Na+ occupancy and then enhances the ionic conductivity of electrolytes. On the other hand, the formed phosphate grain boundary phase with low electronic conductivity prevents the movement of electrons at the grain boundary, reducing the probability that electrons combine with Na+ at the grain boundary to form Na-0, thereby restricting the formation of dendrites along grain boundaries. In addition, the added Sm2O3 and Ho2O3 play the role of fluxing agents to increase the densification of ceramics, further enabling the enhancement of ionic conductivity and restriction of dendrites in the voids. As a result, the obtained NZSP-0.2Sm and NZSP-0.3Ho electrolytes deliver critical current density (CCD) values of 0.85 and 0.65 mA cm(-2), respectively, at room temperature. Application of the obtained electrolytes in Na metal batteries is evaluated by assembling Na3V2(PO4)(3)vertical bar NZSP-0.2Sm/0.3Ho vertical bar Na cells, which deliver high discharge capacity values of 102.6 and 101.8 mAh g(-1) at 0.5 C after 100 cycles with capacity retention ratios of 98.3 and 98.6%, respectively. The presented results indicated that rare earth oxideassisted sintering is an effective route to improve the ionic conductivity and restrict dendrite formation for oxide ceramic solid-state electrolytes.

Gallium-substituted Nasicon Na3Zr2Si2PO12 solid electrolytes

NASICON-structured Na3.1Zr1.95Mg0.05Si2PO12 solid electrolyte for solid-state sodium batteries

Mg-doped NASICON-type electrolyte for rechargeable solid-state sodium-ion batteries

Enhanced electrochemical properties of NASICON-type Na3Zr2Si2PO12 solid electrolytes with Tb3+-ions-assisted sintering

Aliovalent dual element co-assisted strategy to enhance ionic conductivity and stability of NASICON-type solid electrolyte for all-solid-state sodium batteries

Calcium Doped NASICON electrolyte with Graphite Coating for Stable All‐solid‐state Sodium Metal Batteries

Synthesis of High Na + Ion-Conducting NASICON-Based Electrolytes and Insights from Diffraction and Positron Annihilation Lifetime Spectroscopy Studies

Enhanced grain connection and ionic conductivity of Na3.3La0.3Zr1.7Si2PO12 ceramic electrolyte by adding Na2B4O7

Rare Earth Oxide-Assisted Sintered NASICON Electrolyte Composed of a Phosphate Grain Boundary Phase with Low Electronic Conductivity

Enhanced ionic conductivity of Cu-doped NASICON solid electrolyte for solid-state sodium batteries

Recent Advance on NASICON Electrolyte in Solid-State Sodium Metal Batteries

Enhanced ionic conductivity in Na3Zr2Si2PO12 NASICON-type solid electrolytes by adding Mg2+-ions

Enhanced Room-Temperature Na+ Ionic Conductivity in Na4.92Y0.92Zr0.08Si4O12

Enhancing Na-ion conducting capacity of NASICON ceramic electrolyte Na3.4Zr2Si2.4P0.6O12 by NaF sintering aid

Modification of NASICON Electrolyte and Its Application in Real Na-Ion Cells

Bi2O3-Assisted Sintering of Na3Zr2Si2PO12 Electrolyte for Solid-State Sodium Metal Batteries

Zirconia-free NaSICON solid electrolyte materials for sodium all-solid-state batteries

Ce-substituted Nano-Grain Na3Zr2Si2PO12 Prepared by LF-FSP As Sodium-Ion Conductors.

Composite NASICON (Na3Zr2Si2PO12) Solid-State Electrolyte with Enhanced Na+ Ionic Conductivity: Effect of Liquid Phase Sintering

Ce-Substituted Nanograin Na3Zr2Si2PO12 Prepared by LF-FSP as Sodium-Ion Conductors

Sandwiched composite electrolyte with excellent interfacial contact for high-performance solid-state sodium-ion batteries