High‐Temperature Oxidation Behavior of Cr‐Si Alloyed Press‐Hardened Steel in Comparison with 22MnB5 Steel
Tianfang Zhang,Lingyu Wang,Zhao Li,Luning Wang,Fei Wang,Wei Xu
DOI: https://doi.org/10.1002/srin.202300565
IF: 2.1258
2024-01-02
steel research international
Abstract:In the present study, a Cr–Si‐alloyed coating‐free press‐hardened steel (CF–PHS) is investigated and compared with the conventional 22MnB5 steel through a 60 min oxidation experiment at 1000–1200 °C. Compared to the 22MnB5 steel, the CF–PHS exhibits lower weight gain at 1000–1150 °C but a higher weight gain at 1200 °C. In the results, using scanning electron microscopy, energy‐dispersive spectroscopy, and X‐ray diffraction, it is revealed that the outer oxide layer of the CF–PHS consisted of Fe 2 O 3 and Fe 3 O 4 , while its inner oxide layer is enriched with FeCr 2 O 4 and Fe 2 SiO 4 —crucial for the oxidation resistance of the CF–PHS. The outer oxide layer of 22MnB5 comprises Fe 2 O 3 , Fe 3 O 4 , and FeO, while the inner layer contains low concentrations of Cr and Si. The mechanism of superior high‐temperature oxidation resistance of CF–PHS compared to 22MnB5 at 1000–1150 °C reveals that the existence of FeCr 2 O 4 and Fe 2 SiO 4 inhibits the diffusion of Fe 2+ and O 2− , effectively hindering the oxidation progress. Moreover, the oxidation resistance of the CF–PHS at 1200 °C deteriorates owing to the melting of Fe 2 SiO 4 at 1200 °C, which significantly accelerates the diffusion of Fe 2+ and O 2− , thus exacerbating the oxidation of CF–PHS.
metallurgy & metallurgical engineering