Additive Manufacturing of AISI H13 Tool Steel with Combinations of Higher Laser Power and Scan Speed: Microstructural and Mechanical Properties Insights

D. M. Santhoshsarang,S. Narayanaswamy,Gururaj Telasang,K. Divya,Ravi Bathe,G. L. Samuel
DOI: https://doi.org/10.1007/s11665-024-10467-w
IF: 2.3
2024-12-01
Journal of Materials Engineering and Performance
Abstract:AISI H13 tool steel is widely used as a die material in pressure die-casting (PDC) applications. The demonstration of additive manufacturing (AM) of AISI H13 tool steel is gaining commercial interest within the tooling industry, with the objective of enhancing the service life of tools by innovating PDC tools with conformal cooling channels. Thus, in the current study, powder bed fusion using laser beam melting (PBF-LB/M) technology was used to manufacture AISI H13 tool steel using high laser power and scan speed processing parameters. Best parameter combinations termed as P1 (300 W and 1000 mm/s) and P2 (250W and 1200 mm/s) were determined from the single-track experiments and used for further multi-track and multi-layer experiments with suitable hatch spacing and layer thickness of 30 μm. The AM-built H13 tool steel samples were characterized for microstructural and mechanical properties in both as-built and post-build heat treatment (650 °C, 2 h) conditions. In an as-built condition, the microstructure was predominantly dominated by lath martensite with a minor fraction of retained austenite. The observed randomized texture is attributed to the formation of a multitude of martensite blocks with different crystallographic orientations. Substantial enhancements in hardness, reaching 575 ± 20 HV, and tensile properties with an ultimate tensile strength of about 2 GPa, with 8-10 % ductility, were observed in as-built conditions. The underlying mechanisms associated with microstructure formation, texture, and mechanical properties were critically discussed for as-built and post-build heat-treated samples and further compared with conventional AISI H13 tool steel. The calculated build rate for the chosen parameters is around 14 cm 3 /h with theoretical densities of approximately 99.5%.
materials science, multidisciplinary
What problem does this paper attempt to address?