Abstract:The aim of this study is to enhance the plasticity and strength of M2 high-speed steel through electron beam melting (EBM) technology. Therefore, by controlling different melting times to change the energy input, a gradient distribution of grain size and uniform distribution of carbides can be achieved. During the deformation process, the gradient structure causes geometrically necessary dislocations (GND) to accumulate near the boundary of regions in the soft zone, resulting in compressive stress in the soft zone and tensile stress in the hard zone, ultimately achieving heterogeneity-induced (HDI) work hardening. This study is to EBM technology for the design and fabrication of three types of M2 high-speed steel samples, denoted as SS-1, SS-2, and SS-3, utilizing three distinct scanning strategies: single melting, double melting, and a combination thereof. The microstructure and phase evolution of these samples were comprehensively characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron backscatter diffraction (EBSD) techniques. The findings demonstrate that when sample SS-3 was subjected to the combined scanning strategy involving both single melting and double melting approaches, its crystal structure exhibited a gradient distribution along with the presence of back stress during tensile testing. Sample SS-3 achieved an average tensile strength of 1479 MPa with an average elongation rate of 1.8%. This represents an enhancement in average tensile strength by approximately 8.6% compared to sample SS-1 (∼1362 MPa) and a significant increase in average elongation rate by around 20% compared to SS-1 (∼1.44%). The gradient grain structure materials show the microstructure transformation from fine grain to coarse-grain in the same material, thus reducing the stress concentration caused by the change of mechanical properties in each region. The SS-3 sample can maintain significant ductility while improving tensile strength. Consequently, this represents a pivotal direction for the advancement of high-performance structural materials. The conducted experimental studies have demonstrated that geometrically necessary dislocations (GNDs) and their associated strain hardening play a crucial role in enhancing the strength of grain structure materials. Additionally, these are essential to achieve an exceptional synergy between strength and toughness in these materials.

Microstructure and Mechanical Properties of H13 Steel/High-Speed Steel Composites Prepared by Laser Metal Deposition

Development of Powder Metallurgy High Speed Steel

Effect of Laser Cladding Stellite 6-Cr3C2-WS2 Self-Lubricating Composite Coating on Wear Resistance and Microstructure of H13

Microstructure and Mechanical Properties of FeCoCrNiAl + WC Composite Coating Formed by Laser Cladding on H13

Effect of Tungsten Carbide Additions on the Microstructure, Mechanical, and Tribological Properties of M2 High-Speed Steel Matrix Composites

Microstructure evolution and mechanical properties of H13 steel produced by Selective Electron Beam Melting

Microstructures and Mechanical Properties of H13 Tool Steel Fabricated by Selective Laser Melting

Additive Manufacturing of AISI H13 Tool Steel with Combinations of Higher Laser Power and Scan Speed: Microstructural and Mechanical Properties Insights

Assessment of Mechanical Behavior in H13 Tool Steel Synthesized through Electron Beam Melting and Selective Laser Melting Techniques

Laser melting deposited a laminated H13/17–4PH heterostructure alloy to achieve strength-ductility synergy and outstanding high-temperature wear resistance

Improvement of mechanical property of M2 high-speed steel with hetero-microstructure tailored via electron beam melting

Microstructure and Mechanical Properties of Additive Manufactured AISI 410/CoCrFeNiMo High-Entropy Alloy Dissimilar Alloys via Combining Wire-Arc Directed Energy Deposition and Selective Laser Melting Approach

Microstructure, Mechanical, and Corrosion Properties of 304 Stainless Steel-H13 Tool Steel Composite Cold Spray Coatings

A Comparative Study on the Laser Surface Melting and Laser Surface Cladding of H13 Tool Steel

Process-Structure-Property Relationships of AISI H13 Tool Steel Processed with Selective Laser Melting

Laser powder bed fusion of WC-reinforced Hastelloy-X composite: microstructure and mechanical properties

Analysis of interface microstructure and element diffusion of WC-Co-Ni-Fe powder and M2 high-speed steel composite

Microstructure and mechanical properties of H13 tool steel fabricated by high power laser powder bed fusion

Revealing the microstructural evolution and its influence on mechanical properties of heterostructured steel fabricated by laser melting deposition

Effect of Particle Size on Microstructure and Element Diffusion at the Interface of Tungsten Carbide/High Strength Steel Composites

Study on the Microstructure and Performance of the Multi-Field Composite-Assisted Laser Cladding of Nickel-Based Tungsten Carbide Coatings