Laser melting deposited a laminated H13/17–4PH heterostructure alloy to achieve strength-ductility synergy and outstanding high-temperature wear resistance

Hangtao Gao,Jiawang Wu,Yaxiong Guo,Fangping Wang,Tianhai Liao,Jing Zhang,Qibin Liu

DOI: https://doi.org/10.1016/j.jallcom.2024.176861

IF: 6.2

2024-10-10

Journal of Alloys and Compounds

Abstract:To inhibit the cracking behavior induced by the poor ductility of LMD-ed H13 steel, we have adopted a soft/hard laminated composite strategy to achieve a 17–4PH/H13 heterostructure alloy. Also, the effect of its hard-soft interfacial characteristics on tensile properties and high/room-temperature wear resistance has been studied. The research results show that this laminated alloy mainly comprises two alternately stacked martensite layers with a layer width of 350 μm, including lath martensite (H13) and lath martensite (17–4PH). The lath-like martensite layer possesses a high average microhardness value of over 500 HV, far higher than that of LMD-ed 17–4PH steel. Besides, the laminated alloy shows a high σ b (∼1721.59 MPa) with a sufficient δ (∼5.21 %), far higher than that of LMD-ed H13 steel (i.e., σ b ∼1701.41 MPa and δ ∼ 1.27 %), which the fracture mode is mixed by ductile and cleavage fracture. The H13/17–4PH laminated alloy has excellent wear resistance at RT comparable to the LMD-ed H13 steel. Interestingly, the H13/17–4PH laminated alloy maintains low friction coefficients and wear rates at 600 °C. Specifically, its high-temperature wear rate (22.28×10 −6 mm 3 N −1 ·m −1 ) is one-eighth as low as that of LMD-ed H13 steel (157.17×10 −6 mm 3 N −1 ·m −1 ). The above results provide a reference for re-manufacturing die steels in industrial applications of high-temperature wear resistance.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering