Abstract:Owing to their superior high-temperature stability, SiC-based ceramic matrix composites are widely used in turbine engine components for launch vehicles and other applications in the aerospace industry. However, because of the deterioration that occurs in these materials in high-temperature wet operating environments, researchers have developed environmental barrier coating technologies to protect the substrate. In this study, a top coat was prepared using Yb2SiO5 and Yb2Si2O7 as the third-generation coating of a rare-earth silicate with high thermal, chemical, and mechanical stability in high-temperature environments above 1400 °C. A new bond coat was prepared, incorporating Si, whose thermal expansion coefficient is similar to that of the SiC substrate, and Hf, which is expected to significantly contribute to high-temperature stability. The coating was prepared by suspension plasma spraying rather than atmospheric plasma spraying to realize a fine coating particle structure; to densify the coating layers, secondary densification coatings were created using ytterbium (III) nitrate pentahydrate (Yb(NO3)3∙5H2O) and tetraethyl orthosilicate (C8H20O4Si). The prepared specimens were measured in terms of weight change and weight change ratio with respect to temperature under high-temperature flames (1400 ℃ and 1700 ℃). After the secondary densification coating, the microstructure of the specimen was observed to be denser and the surface layer of the coating exhibited crystallinity. For the tested samples, a decrease in weight was observed. The largest weight loss was observed under the 1700 ℃ flame.

High-temperature performance of thermal environmental barrier coatings in 90%H2O-10%O2 conditions at 1475 °C

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

High-temperature performances of Si-HfO2-based environmental barrier coatings via atmospheric plasma spraying

Cyclic oxidation performances of new environmental barrier coatings of HfO2-SiO2/Yb2Si2O7 coated SiC at 1375 °C and 1475 °C in the air environment

Oxidation resistance and thermal shock behavior of tri-layer Si/Si–Yb2SiO5/Yb2SiO5–SiC environmental barrier coatings at 1300 °C

Thermal durability of ytterbium silicate environmental barrier coating prepared by suspension plasma spray

Thermal cycling and steam corrosion behavior of Yb3Al5O12‐based multilayered environmental barrier coatings for SiCf/SiC

Thermal cycle and water oxygen performance of multi-layered Y3Al5O12/Yb2SiO5/Yb2Si2O7 thermal/environmental barrier coatings

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Characterization of Yb2SiO5-based environmental barrier coating prepared by plasma spray–physical vapor deposition

Oxidation behavior and cracking evolution of atmospheric plasma spraying Si and 60Si-40HfO2 bond coats at 1400 °C

Properties evaluation and failure behaviour of plasma sprayed Y4Hf3O12 for thermal barrier coating applications

Thermophysical properties and cyclic lifetime of plasma sprayed SrAl 12 O 19 for thermal barrier coating applications

Oxidation behavior and interface evolution of tri-layer Si/Yb2SiO5/LaMgAl11O19 thermal and environmental barrier coatings under isothermal heat treatment at 1300 °C

Evolution mechanism of the microstructure and mechanical properties of plasma-sprayed yttria-stabilized hafnia thermal barrier coating at 1400 °C

Thermal shock resistance and bonding strength of tri-layer Yb2SiO5/mullite/Si coating on SiCf/SiC composites

High-temperature interface stability of tri-layer thermal environmental barrier coatings

Phase composition evolution and oxidation behavior of atmospheric plasma spraying Si and Si-HfO 2 bond coats at 1300 °C

Structural and Phase Transformations in Plasma-Spray ZrB2–SiC–AlN Coatings on a C/C–SiC Substrate After High-Temperature Thermal Cyclic Heating

Oxidation resistance of SiCf/SiC composites with three-layer environmental barrier coatings up to 1360 °C in air atmosphere

Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests