Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Oxidation behavior and cracking evolution of atmospheric plasma spraying Si and 60Si-40HfO2 bond coats at 1400 °C

Phase composition evolution and oxidation behavior of atmospheric plasma spraying Si and Si-HfO 2 bond coats at 1300 °C

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

Effect of HfO2 framework on steam oxidation behavior of HfO2 doped Si coating at high temperatures

High-temperature performance of thermal environmental barrier coatings in 90%H2O-10%O2 conditions at 1475 °C

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

High-temperature performances of Si-HfO2-based environmental barrier coatings via atmospheric plasma spraying

Oxidation mechanism of SiC coated layer in air atmosphere at 1400°C

Oxidation Resistance of a Si-TiSi2-MoSi2-TiB2-CaSi2 Coating on a Cf/C-SiC Substrate in High-Speed High-Enthalpy Air Plasma Flows

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Oxidation behavior of AlCoCrFeNiSi x high entropy alloy bond coatings prepared by atmospheric plasma spray

Cyclic oxidation performances of new environmental barrier coatings of HfO2-SiO2/Yb2Si2O7 coated SiC at 1375 °C and 1475 °C in the air environment

Preparation, properties and high-temperature oxidation resistance of MoSi2-HfO2 composite coating to protect niobium using spent MoSi2-based materials

Preparation of MoSi2-modified HfB2-SiC ultra high temperature ceramic anti-oxidation coatings by liquid phase sintering

Oxidation Behavior of Dense SiC Coating in Water Vapor and Its Mixed Atmosphere with Air

Structural and Phase Transformations in Plasma-Spray ZrB2–SiC–AlN Coatings on a C/C–SiC Substrate After High-Temperature Thermal Cyclic Heating

Oxidation Behavior of (Mo,Hf)Si2-Al2O3 Coating on Mo-Based Alloy at Elevated Temperature

High Temperature Oxidation Behavior of SiC Coating Materials

Effect of Mild Oxidation on Ablation Properties of ZrSiO4 Coating Prepared by Supersonic Atmospheric Plasma Spraying on Carbon/Carbon Composites

Preparation and characterization of molybdenum disilicide coating on molybdenum substrate by air plasma spraying