Abstract:The external ambient temperature plays a crucial role in influencing the hydration process of cemented paste backfill (CPB), causing notable variations in overall structure and physicalmechanical properties. To precisely analyze mechanical properties under different curing temperatures, a uniaxial compression strength (UCS) experiment was conducted. A real-time data acquisition system was established to monitor temperature, volumetric water content, and resistivity. Hydration heat measurement and low-field nuclear magnetic resonance (NMR) experiments were performed to analyze the hydration mechanism and the correlation between mechanical properties and thermal effects during the consolidation period. The study revealed that the relationship between UCS, elastic modulus, and curing temperature can be quantitatively characterized using polynomial functions. The mechanical parameters reach their peak values at a curing temperature of 40 degree celsius. However, exceeding 40 C leads to excessively rapid hydration rates, causing a decrease in hydration degree, and extremely high hydration rates result in reduced microstructure compactness. Under different curing temperature conditions, CPB exhibits substantial temperature effects in terms of volumetric water content, electrical resistivity, hydration heat, and NMR data, effectively characterizing the hydration mechanism. The hydration reaction unfolds through stages: initial induction, accelerated development, decelerated development, stable development, and hardening formation. As the curing temperature rises, the completion times of each stage exhibit a significant exponentially decreasing trend. Moreover, the application of the GA-BP neural network algorithm has unveiled inherent patterns between the monitoring results of CPB's hydration process and its macroscopic strength. Computed results show that the relative errors in predicting strength at various curing temperatures are all less than 0.1 %.

Physio-chemical effects on the temperature-dependent elasticity of cement paste during setting

Long-term Thermal Performance of Oil Well Cement Modified by Silica Flour with Different Particle Sizes in HTHP Environment

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

Influence of elevated curing temperature on the properties of cement paste and concrete at the same hydration degree

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Effect of Temperature on the Early-age Hydration and Setting Behaviour of Mixes Containing GGBS

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

The Effect of Curing Temperature on the Properties of Shrinkage-Compensated Binder

Experimental study of pure Class G cement hydration up to 150oC and 50MPa

Effects of Curing Temperature on Rheological Behaviour and Compressive Strength of Cement Containing GGBFS

THE EFFECTS OF HIGH TEMPERATURE CURING ON HYDRATION REACTION AND STRENGTH DEVELOPMENT OF CEMENT PASTE CONTAINING SILICA FUME AT LOW WATER BINDER RATIO

Hydration Mechanism and Mechanical-Thermal Correlation of Cemented Paste Backfill under Different Curing Temperatures

Study on microstructure deterioration of cement paste exposed to elevated temperature

Influence of Early Hydration Process on the Hydrostatic Pressure Change of Cement Pastes at Different Temperatures

Effect of Temperature on Pore Structure and Strength of Concrete

Investigating the effect of polycarboxylate-ether based superplasticizer on the microstructure of cement paste during the setting process

Effects of Tuff Powder on the Hydration Properties of Cement-Based Materials under High Temperature

Variations of Yield Stress of Fresh Cement Pastes in the Presence of Superplasticizer Highlighted by A Hydration Index

Effect of High Temperature on Compressive Strength and Microstructure of Cement Paste Modified by Micro- and Nano-calcium Carbonate Particles

Mechanical Characteristics and Macro–Microscopic Response Mechanisms of Cemented Paste Backfill under Different Curing Temperatures

Effects of curing temperature on cement-stabilized soils