Abstract:The influence of different wind speeds and sealed curing time on early-age shrinkage of cement paste was investigated. The 72-h early-age total shrinkage of cement paste after sealed curing for 0 h, 3 h, 6 h, 9 h, 12 h, and 24 h starting from the initial setting time under different wind speeds was studied. Water loss, autogenous shrinkage, tensile strength, pore size distribution (PSD) and hydration degree were measured. Elastic modulus, cracking strain, and radius of the pores where the meniscus forms were calculated based on the data obtained. For mixtures that did not undergo sealed curing, the wind speed could considerably increase the drying shrinkage and total shrinkage of the cement paste. The wind speed also reduced the early tensile strength, hydration degree, and elastic modulus of the cement paste. Within 1 day, the cracking strain was reduced by wind speed. According to the experimental data, a fitting formula for the early total shrinkage of cement paste is proposed, and the wind speed influencing factor beta(w) is also proposed for the first time. Considering the PSD and water loss to study the mechanism of early drying shrinkage of cement paste, we found that there is a good correlation between r(s) and drying shrinkage. The exponential formula is given between r(s) and drying shrinkage. For mixtures with sealed curing, the total shrinkage and water loss decreased with increasing sealed curing time. However, the effects of water loss at different stages on drying shrinkage were different. Water evaporation in the early stage led to more drying shrinkage than water evaporation in the later stage. Sealed curing also weakened the increasing effect of wind speed on total shrinkage, so that at the same wind speed, the shrinkage increment was considerably reduced. After analysis and comparison, it was found that it is economical and reasonable to adopt sealed curing for 6 or 9 h, which can effectively decrease the early total shrinkage and improve the cracking strain of the cement paste in the wind environment. (C) 2020 Elsevier Ltd. All rights reserved.

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Influence of Superplasticiser on Early Shrinkage and Total Shrinkage of Concrete

Effect of Different Wind Speeds and Sealed Curing Time on Early-Age Shrinkage of Cement Paste

Is Early Drying Shrinkage Still Determined by the Mesopore Content? A Case Study of Cement Paste with Minerals

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Influence of Early-age Curing Time on Shrinkage of Concrete

Influence of Superplasticizer and Shrinkage-Reducing Admixtures on Early Age Shrinkage of Concrete

Influence of Recycled Cement Paste Powder on Early-Age Plastic Shrinkage and Cracking of Cement-Based Materials

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Effect of Beginning Curing Time on Early Age Shrinkage of Concrete

Rheological Behaviors of Fresh Cement Pastes with Polycarboxylate Superplasticizer

Variations of Yield Stress of Fresh Cement Pastes in the Presence of Superplasticizer Highlighted by A Hydration Index

Influence of Amphoteric Polycarboxylate Copolymer Superplasticizer on Early Hydration of Portland Cement

Development of Shrinkage and Internal Moisture in Cement Paste,Mortar and Concrete at Early Age

Hydration Mechanism and Mechanical-Thermal Correlation of Cemented Paste Backfill under Different Curing Temperatures

Experimental study on early shrinkage and later expansion of concrete under a simulated geothermal environment

Autogenous deformation and coefficient of thermal expansion of early-age concrete: Initial outcomes of a study using a newly-developed Temperature Stress Testing Machine

Effects of Admixtures and SRA on Early Age Shrinkage of Concrete