Abstract:Cement-based materials, especially those with low water-cement ratios, often experience premature cracking due to plastic shrinkage in the early curing stages. In this study, the development mechanism of early-age plastic shrinkage of cement paste, and the crack shrinkage control effect of recycled cement paste powder on cement paste, was quantitatively investigated using non-contacting two-dimensional digital image technology. The influence of different replacement rates (5%, 10%, 20% and 30%) of recycled cement paste powder on the major principal strain and crack patterns of cement paste was investigated. Furthermore, the mechanism of recycled cement paste powder on the early-age plastic shrinkage of cement-based materials was explored. The results show that the addition of recycled cement paste powder could suppress the early-age plastic shrinkage of cement paste. An appropriate replacement ratio (10%) of recycled cement paste powder shows a 33.3% time delay in crack appearance and a 28.0% reduction in the major principal strain. However, the higher replacement ratio of 30% shows an adverse effect on the major principal strain, with an increase of 35.1%. The core mechanism of the appropriate recycled cement paste powder on plastic shrinkage reduction lies in its porous nature, which allows for water absorption and release and regulates the moisture state inside the pores. This quantitative research of the major principal strain development of the early-age plastic shrinkage of cement paste can facilitate a better understanding of plastic shrinkage reduction in recycled cement paste powder on cement paste.

Influence of Superplasticiser on Early Shrinkage and Total Shrinkage of Concrete

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Influence of Superplasticizer and Shrinkage-Reducing Admixtures on Early Age Shrinkage of Concrete

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Influence of Early-age Curing Time on Shrinkage of Concrete

Negative Influence of Superplasticisers on Shrinkage and Cracking of Concrete

Effect of Beginning Curing Time on Early Age Shrinkage of Concrete

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

A study on early shrinkage of recycled concrete

Effects of Admixtures and SRA on Early Age Shrinkage of Concrete

Experimental study on effects of polypropylene fiber on early-age shrinkage in concrete

Influence of Shrinkage Retarder on Early Self-Shrinking of Concrete

Influence of Shrinkage Reduce Agent on Early Age Autogenous Shrinkage of Concrete

Property of Water-Reducing and Crystallization on Superplasticize of the Concrete

Influence of Recycled Cement Paste Powder on Early-Age Plastic Shrinkage and Cracking of Cement-Based Materials

Influence of Relative Humidity on Shrinkage of Mortar and Concrete

Effect of Super Absorbent Polymer mixing method on shrinkage performance of cast-in-place concrete confined by existing concrete

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Shrinkage and Cracking of Cement Composites Containing Internal Curing Stuff

Research Status of Shrinkage-Reducing Polycarboxylate Superplasticizer