Abstract:In order to study the effect of polycarboxylate superplasticizer (PCE) on the microstructure and strength characteristics of tailings paste, a total of 6 tailings paste combinations including 2 cement-sand ratios (20%, 40%) and 3 water reducer dosages (0, 0.40%, 0.80%) were investigated based on the indoor microstructure test (porosity measurement, XRD test, and SEM observation) and mechanical properties method. The strength of test blocks at different ages was obtained by numerical simulation. The results showed that: 1) The water reducer can effectively reduce the porosity of the tailings paste, and the reduction effect was more significant in the condition of high cement-sand ratios. Meanwhile, high cement-sand ratio is conductive to generate more beneficial hydrates such as portlandite; 2) Compared with the significant effect of cementitious agent on the tensile strength σ t of the paste, the effect of water reducer on σ t is weak. Accordingly, the σ t of the tailings paste is much more sensitive to cementitious agent than water reduce; 3) SEM images show that the better ratio of slurry containing polycarboxylic acid superplasticizer has more C-S-H cementitious content, smaller pore size and shorter molecular chain between particles, indicating that the particles are more encapsulated and the early strength is improved. 4) The incorporation of water reducer enhancement was particularly significant under the condition of triaxial compression. However, the presence of water reducer did not change its deformation characteristics, when the confining pressure is low, the strain softening appears; and when the confining pressure is high, it transforms to strain hardening. The peak strain ε 0 and the confining pressure σ 3 had a linear relationship; 5) The strength of the paste was significantly affected by the confining pressure σ 3 under different conditions. The peak intensity σ 1 and the confining pressure σ 3 satisfied a linear relationship, while the residual strength σ r and the confining pressure σ 3 satisfied a quadratic polynomial fitting relationship. The strength parameters cohesion c and internal friction angle φ were both positively correlated with the water reducer dosage.

Property of Water-Reducing and Crystallization on Superplasticize of the Concrete

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Study on the effect of cementitious capillary crystalline waterproofing materials on enhancing concrete anti-carbonization property

Influence of Superplasticiser on Early Shrinkage and Total Shrinkage of Concrete

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Study On The Synthesis And Properties Of Water Soluble Superplasticizer With Side Branch Poly(Ethylene Glycol) Methyl Ether

Effect of Functional Superplasticizers on Concrete Strength and Pore Structure

Effect of Adding Electrolyte in Cement Paste on the Dispersing Force of Polycarboxylate-Type Superplasticizer

Effects of Mineral Admixtures and Superplasticizer on Controlling Hydration Heat of Cementitious Materials

Synthesis and characterization on anti-clay polycarboxylate superplasticizer in concrete

Effects of Polycarboxylate Superplasticizers on Fluidity and Early Hydration in Sulfoaluminate Cement System

Synthesis and Performance of Polycarboxylate Superplasticizer with Viscosity-Reducing and Low-Shrinkage Properties for Fair-Faced Concrete

Effect of dose and types of the water reducing admixtures and superplasticizers on concrete strength and durability behaviour: a review

Effect of the Alkyl Density of Acrylic Acid Ester on the Viscosity-Reducing Effect of Polycarboxylate Superplasticizer

Experimental Research on the Microstructure and Strength Characteristics of Tailings Paste Containing Wate Reducer

Characteristics and Engineering Application of Zeolite Plastic-keeping Water Reducer

Effect of Naphthalene-Based Superplasticizer and Polycarboxylic Acid Superplasticizer on the Properties of Sulfoaluminate Cement

Improving function of super absorbent polymer on early cracking of concrete under high temperature and dry environment

Shrinkage and Cracking Behavior of High Performance Concretes Containing Chemical Admixtures

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers