Abstract:The hydration process and compressive strength and flexural strength development of sulphate-resistant Portland cement (SRPC) curing at 20 °C, 40 °C, 50 °C, and 60 °C were studied. In addition, MIP, XRD, SEM, and a thermodynamic simulation (using Gibbs Energy Minimization Software (GEMS)) were used to study the pore structure, the types, contents, and transformations of hydration products, and the changes in the internal micro-morphology. The results indicate that, compared with normal-temperature curing (20 °C), the early compressive strength (1, 3, and 7 d) of SRPC cured at 40~60 °C increased by 10.1~57.4%, and the flexural strength increased by 1.8~21.3%. However, high-temperature curing was unfavorable for the development of compressive strength and flexural strength in the later period (28~90 d), as they were reduced by 1.5~14.6% and 1.1~25.5%, respectively. With the increase in the curing temperature and curing age, the internal pores of the SRPC changed from small pores to large pores, and the number of harmful pores (>50 nm) increased significantly. In addition, the pore structure was further coarsened after curing at 60 °C for 90 d, and the number of multiple harmful pores (>200 nm) increased by 17.9%. High-temperature curing had no effect on the types of hydration products of the SRPC but accelerated the formation rate of hydration products. The production of the hydration products C-S-H increased by 13.5%, 18.6%, and 22.8% after curing at 40, 50, and 60 °C for 3 d, respectively. The stability of ettringite (AFt) reduced under high-temperature curing, and its diffraction peak was not observed in the XRD patterns. When the curing temperature was higher than 50 °C, AFt began to transform into monosulfate, which consumed more tricalcium aluminate hydrate and inhibited the formation of “delayed ettringite”. Under high-temperature curing, the compactness of the internal microstructure of the SRPC decreased, and the distribution of hydration products was not uniform, which affected the growth in its strength during the later period.

Study on microstructure deterioration of cement paste exposed to elevated temperature

Long-term Thermal Performance of Oil Well Cement Modified by Silica Flour with Different Particle Sizes in HTHP Environment

Deterioration of Cement-Fly Ash Composite Binder Materials Exposed to Elevated Temperature

Effect of High Temperature on Compressive Strength and Microstructure of Cement Paste Modified by Micro- and Nano-calcium Carbonate Particles

Experimental Study of Micro/macro Crack Development and Stress–strain Relations of Cement-Based Composite Materials at Elevated Temperatures

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

Microstructural study of concrete performance after exposure to elevated temperatures via considering C–S–H nanostructure changes

Deterioration Mechanism of Concrete under Long-Term Elevated Temperature in a Metallurgic Environment: A Case Study of the Baosteel Company

Microstructure and Mechanical Properties of High-Toughness Fiber-Reinforced Cementitious Composites after Exposure to Elevated Temperatures

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

The impact of changes in pore structure on the compressive strength of sulphoaluminate cement concrete at high temperature

Effect of Temperature on Pore Structure and Strength of Concrete

Deterioration of performances and structures of cement pastes under the action of thermal cycling fatigue

Development And Design Of Composite Cementitious Material At Long-Time Circular Elevated Temperature In Metallurgy Environment

Investigation on physicochemical and piezoresistive properties of smart MWCNT/cementitious composite exposed to elevated temperatures

The effect of extensive heat exposure on the mechanical properties of polymer-modified sulfoaluminate cement repair mortar

Performance Degradation and Microscopic Analysis of Lightweight Aggregate Concrete after Exposure to High Temperature

Study on the Strength and Hydration Behavior of Sulfate-Resistant Cement in High Geothermal Environment

Insight into Class G Wellbore Cement Hydration and Mechanism at 150 °C Using Molecular Dynamics

The effects of high temperature heating on the gas permeability and porosity of a cementitious material

Effect of micro‐structural changes on concrete properties at elevated temperature: Current knowledge and outlook