Abstract:Ultra-high performance concrete (UHPC) tends to crack and flake at high temperature, which causes the structure to lose its overall stability and collapse, posing a serious threat to people's lives and property safety. In this study, by selecting the cementitious material and the high-temperature resistant aggregate, a new type of high-temperature resistant ultra-high performance concrete (HTR-UHPC) was successfully developed. The high temperature resistance tests of HTR-UHPC were systematically carried out at 5 different temperatures (20 °C, 250 °C, 500 °C, 750 °C, 1000 °C). The compressive and axial tensile properties of the specimens were investigated after high temperatures, and the compressive and tensile stress–strain curves were obtained. High-temperature products and internal structures were tested by scanning electron microscopy (SEM) and X-ray diffractometry (XRD), respectively, and the microscopic mechanisms were revealed. The results showed that the mechanical properties of the HTR-UHPC had been significantly improved after heating at 500 °C, 750 °C, and 1000 °C. When heated to 500 °C, the compressive and tensile strength of HTR-UHPC retained 106 and 88% of the unheated status, respectively. While the structure of traditional UHPC was damaged, the compressive and tensile strength retained only 90 and 76%. Moreover, when heated to 750 °C, the HTR-UHPC still maintained structural integrity. The residual compressive and tensile strength could still reach 115.83 and 6.17 MPa. During the hydration process, the HTR-UHPC did not generate calcium hydroxide, and the failure stress caused by high-temperature dehydration was small. At the same time, the ability of late crystal transition to reduce strength was suppressed by the addition of mineral admixtures, which enabled the formation of cracks and pores to be effectively suppressed. The stability and mechanical properties of the structure were maintained. Overall, these findings offer valuable insights into the influence of cementitious material system and high-temperature resistant aggregate on the mechanical properties of HTR-UHPC.

Development And Design Of Composite Cementitious Material At Long-Time Circular Elevated Temperature In Metallurgy Environment

Deterioration Mechanism of Concrete under Long-Term Elevated Temperature in a Metallurgic Environment: A Case Study of the Baosteel Company

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

Multiscale Prediction of Thermal Damage for Hybrid Fibers Reinforced Cementitious Composites Blended with Fly Ash at High Temperatures

Long-Term Performance of External Bonding under Moisture and Temperature Effects

A review of high temperature properties of cement based composites: Effects of nano materials

Experimental on the Behavior of Beams Strengthened by Polymer-modified Fiber Cement Mortar Under Hydrothermal Conditions

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Optimal Design and Performance of Concrete with Function Component in Marine Environment

Tailoring the Thermal and Mechanical Properties of Lightweight Cement-Based Composites by Macro and Micro Fillers

Deterioration of Cement-Fly Ash Composite Binder Materials Exposed to Elevated Temperature

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Mechanical properties and micro-structure analysis of concrete adding high performance composite cementious material

Hydration and pore structure characteristics of concrete incorporating internal curing materials in a dry and large-temperature-difference environment

Study on microstructure deterioration of cement paste exposed to elevated temperature

Optimal Design of Multi-Layer Structure Composite Containing Inorganic Hydrated Salt Phase Change Materials and Cement: Lab-scale Tests for Buildings

The effect of extensive heat exposure on the mechanical properties of polymer-modified sulfoaluminate cement repair mortar

Study on Mechanical and Microscopic Properties of Fly Ash Cement-Based Materials in High Geothermal Environment

Thermal Stability Study of Fiber-Reinforced Cementitious Composites with High Ductility under High-Temperature Casting

Study on preparation and mechanical properties of a new type of high-temperature resistant ultra-high performance concrete

Study on the Constitutive Relationship between Ordinary Concrete and Nano-Titanium Dioxide-Modified Concrete at High Temperature