Efficient Extraction of Lithium from Calcined Kaolin Lithium Clay with Dilute Sulfuric Acid

Wenlin Zhong,Lang Yang,Feng Rao,Liangzhou Tong,Haipeng Feng

DOI: https://doi.org/10.3390/min14040359

IF: 2.5

2024-03-30

Minerals

Abstract:In this study, the structure and phase transition of kaolin lithium clay at different calcination temperatures were studied and discussed; subsequently, the effects of Li leaching with sulfuric acid under various factors were investigated in detail. The experimental results indicated that an optimal Li leaching rate of 81.1% could be achieved when kaolin lithium clay was calcined at 600 °C for 1 h, followed by leaching with 15.0% sulfuric acid at 80 °C for 2 h. The TG-DSC, XRD, and SEM analyses showed that the layered structure of the clay was not destroyed during the leaching and calcination processes. During the process of calcination, kaolinite was converted to metakaolinite via dehydroxylation. During the process of leaching, the Al on the surface of the metakaolinite was dissolved by sulfuric acid, resulting in the destruction of the Al-O structure; then, Li+ was exchanged for H+ to the surface of the mineral and entered the solution under the action of diffusion. The leaching kinetics showed that the leaching process was controlled by a diffusion model, and the activation energy (Ea) was 41.3 kJ/mol. The rapid extraction of Li from calcined kaolin lithium clay with sulfuric acid leaching offers a high-efficiency, low-energy-consumption strategy for the utilization of new lithium resources.

geochemistry & geophysics,mineralogy,mining & mineral processing