Abstract:The idea of intragranular in-situ reactions results in the proliferation of nanoreinforcements in a metal matrix composite. In this regard, high-content multi-component hybrid-reinforced 6061Al composites were synthesized in-situ from template reaction between TiO 2 -decorated carbon nanotubes (CNTs) and the matrix by flake powder metallurgy. TiO 2 nanoparticles were introduced with the help of low-amount of CNT as carrier. The total content of reinforcements increased from 3.4 wt% to ∼17.35 wt% when TiO 2 -decorated CNTs were completely reacted with the matrix, producing Al 4 C 3 /Al 4 O 4 C/Al 3 Ti/Al 2 O 3 compounds during high temperature sintering/extrusion. The as-fabricated hybrid composite exhibited outstanding mechanical properties of high tensile strength (570 MPa) and high Young's modulus (98.6 GPa) at room temperature, which were 105 % and ∼33 % higher than those of 6061Al matrix. Furthermore, the tensile strength of the hybrid-reinforced composite reached 211 MPa at 300 °C, which is about 270 % higher than the matrix. The remarkable mechanical properties were attributed to the in-situ formation of multi-components/nanophases with superior mechanical properties and high thermal stabilities. The results indicate that uniform incorporation of high-content nanophases through the in-situ reaction of nanoparticle-decorated CNTs is a promising path to produce high-performance nanocomposites and can be applied to other composite systems.

Using direct high-pressure torsion synthesis to produce aluminium matrix nanocomposites reinforced with carbon nanotubes

Fabrication of High-Content Hybrid-Reinforced Al Nanocomposites by In-Situ Reaction of TiO2-decorated CNTs and Matrix

Fabrication of high-content hybrid-reinforced Al nanocomposites by in-situ reaction of TiO 2 -decorated CNTs and matrix

Processing and Properties of Carbon Nanotubes Reinforced Aluminum Composites

Fabrication of Ultrafine Grained Al/Mg Multilayered Composite by High Pressure Torsion

Microstructures and properties of graphene nanoplatelets reinforced Cu/Ti3SiC2/C nanocomposites with efficient dispersion and strengthening achieved by high-pressure torsion

Preparation and characterization of carbon nanotubes/aluminum matrix composites

Effect of Increasing the Strength of Aluminum Matrix Nanocomposites Reinforced with Microadditions of Multiwalled Carbon Nanotubes Coated with TiC Nanoparticles

In-situ Homogeneous Synthesis of Carbon Nanotubes on Aluminum Matrix and Properties of Their Composites

Strength enhancement of an aluminum alloy through high pressure torsion

Micro/Nanostructure and Tribological Characteristics of Pressureless Sintered Carbon Nanotubes Reinforced Aluminium Matrix Composites

Influence of Processing Parameters on the Mechanical Properties of HPT-Deformed Nickel Carbon Nanotube Composites

The nanoscale mechanisms of strengthening and ductility enhancement in an Al–Mg–Si–Mn alloy on processing by high-pressure torsion

Effect of Secondary Processing and Nanoscale Reinforcement on the Mechanical Properties of Al-TiC Composites

Mechanical Properties and Interfacial Analysis of Aluminum Matrix Composites Reinforced by Carbon Nanotubes with Diverse Structures

Nano-scale Reinforcements and Properties of Al-Si-Cu Alloy Processed by High-Pressure Torsion

Reinforcement of Alumina Matrix with Multi-Walled Carbon Nanotubes

Effects of (tib2 + ZrB2) Nanoparticles on Microstructure and Properties of 7055al Matrix Composites

On the reinforcement homogenization in CNT/metal matrix composites during severe plastic deformation

Effect of Carbon Nanotubes and High Temperature Extrusion on the Microstructure Evolution of Al-Cu Alloy

Investigation on the Reinforcement of Multi-Walled Carbon Nanotubes on Alumina Matrix